Nickel–Cobalt Bimetal Hierarchical Hollow Nanosheets for Efficient Oxygen Evolution in Seawater

Rongzheng An,Guoling Li,Zhiliang Liu
DOI: https://doi.org/10.3390/ma17102298
IF: 3.4
2024-05-14
Materials
Abstract:The electrochemical splitting of seawater is promising but also challenging for sustainable hydrogen gas production. Herein, ZIF-67 nanosheets are grown on nickel foam and then etched by Ni2+ in situ to obtain a hierarchical hollow nanosheets structure, which demonstrates outstanding OER performance in alkaline seawater (355 mV at 100 mA cm−2). Diven by a silicon solar panel, an overall electrolysis energy efficiency of 62% is achieved at a high current of 100 mA cm−2 in seawater electrolytes. This work provides a new design route for improving the catalytic activity of metal organic framework materials.
materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper attempts to address the problem of efficiently performing electrochemical water splitting in seawater to produce hydrogen. Specifically, the paper focuses on how to enhance the catalytic activity and stability of the oxygen evolution reaction (OER) in alkaline seawater electrolytes. This goal is achieved by synthesizing nickel-cobalt bimetallic materials with a layered hollow nanosheet structure (NiCoLDH) and loading them onto nickel foam (NiCoLDH/NF). ### Main Issues: 1. **Enhancing Catalytic Activity**: In natural seawater, due to the presence of chloride ions, the chlorine evolution reaction (CER) can initiate at the anode. This requires the OER catalyst to achieve high current density output at an overpotential below 480 mV to prevent the formation of hypochlorite. Therefore, it is necessary to develop efficient, low-cost, and corrosion-resistant catalysts to improve the feasibility of seawater hydrogen production technology. 2. **Improving Catalyst Structure and Performance**: Traditional metal-organic framework materials (TMOF), although rich in metal centers and microporous structures, still need improvement in catalytic activity. The paper introduces nickel ions (Ni2+) to modulate the valence state of cobalt (Co) and optimize the local electronic structure of the active centers, thereby enhancing catalytic activity. 3. **Performance Verification in Practical Applications**: The paper not only tests the performance of the catalyst under laboratory conditions but also assembles a two-electrode electrolyzer driven by silicon solar cells to verify its application potential under real conditions, especially for overall water splitting in natural seawater. ### Solutions: - **Material Design**: By growing ZIF-67 nanosheets on nickel foam and then in-situ etching with nickel ions (Ni2+), a NiCoLDH/NF catalyst with a layered hollow nanosheet structure is obtained. - **Performance Testing**: The OER performance of the catalyst was tested in 1 M KOH electrolyte and compared with commercial catalyst RuO2. The results showed that NiCoLDH/NF has a lower overpotential and higher catalytic activity. - **Practical Application**: Long-term stability tests were conducted in natural seawater, and a two-electrode electrolyzer driven by silicon solar cells was used to verify its efficiency and stability under practical conditions. ### Conclusion: The paper successfully synthesized a NiCoLDH/NF catalyst with a layered hollow nanosheet structure and demonstrated its excellent OER performance and long-term stability in alkaline seawater electrolytes. Additionally, the catalyst showed high electrolysis efficiency and good durability in practical applications, providing new insights for the development of seawater hydrogen production technology.