Al3+ Introduction Hydrated Vanadium Oxide Induced High Performance for Aqueous Zinc‐Ion Batteries

Jing Xu,Yu Zhang,Chenfan Liu,Huanhuan Cheng,Xuanxuan Cai,Dianzeng Jia,He Lin

DOI: https://doi.org/10.1002/smll.202204180

IF: 13.3

2022-10-15

Small

Abstract:The introduction of Al3+ is predicted to effectively reduce the Zn2+ migration barrier by the theoretical calculations. Based on the theoretical calculations, Al0.34V5O12·2.4H2O nanoribbons are synthesized by hydrothermal introduction of Al3+, and demonstrate excellent electrochemical properties (407.8 mAh g−1 at 0.2 A g−1 and 176.3 mAh g−1 after 2000 cycles at 20 A g−1). Aqueous zinc ion batteries are a promising alternative secondary battery technology due to their excellent safety and environmental friendliness. Vanadium‐based compounds as a highly promising class of cathode materials still suffer from structural collapse and slow kinetics. Studies have shown that metal ion pre‐introduction is an effective method to solve these problems and enhance battery performance. Here, the introduction of Al3+, Cr3+, Cu2+ and Fe3+ is found to effectively reduce the migration energy barrier of Zn2+ with the density functional theory calculations, while Al3+ exhibits the best induction effects. Subsequently, Al0.34V5O12·2.4H2O (AlVOH) nanoribbons are synthesized by hydrothermal introduction of Al3+, demonstratin excellent electrochemical properties (407.8 mAh g‐1 at 0.2 A g‐1 and 176.3 mAh g‐1 after 2000 cycles at 20 A g‐1). By further compounding with redox graphene (rGO), AlVOH/rGO exhibits high capacitance and specific capacity (460.4 mAh g‐1 at 0.2 A g‐1 and 180.6 mAh g‐1 after 2000 cycles at 20 A g‐1). In addition, it is found that the introduction of metal ions adjusts the structural water content of the material. Especially, the introduction of Al3+ can increase the interlayer structural water content and make the electrochemical properties of the material more stable.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology