Solidification and stabilization of heavy metals in medical waste ash through alkali activation

Faris Matalkah,Ayshah Fayyad,Idrees Al-Momani,Faris MatalkahAyshah FayyadIdrees Al-Momania Department of Civil Engineering,Yarmouk University,Irbid,Jordanb Department of Earth and Environmental Sciences,Yarmouk University,Irbid,Jordanc Department Chemistry,Yarmouk University,Irbid,Jordan
DOI: https://doi.org/10.1080/19648189.2024.2331559
2024-03-22
European Journal of Environmental and Civil engineering
Abstract:In the present work, medical waste ash was used as an aluminosilicate precursor to produce a geopolymer binder with stabilised heavy metals. The ash was initially calcined at a temperature of 800 °C for two hours to reduce the organic content. Calcined kaolin and medical waste ash were used as precursors to produce the geopolymer binder and sodium silicate and calcium oxides were used as alkaline activators. The effect of curing temperature (23, 60, and 100 °C) and the calcium oxide addition (0, 5, and 10%) on the geopolymer properties were evaluated. Eighteen geopolymer samples were prepared and evaluated for immobilizing heavy metals through the Toxicity Characteristic Leaching Procedure (TCLP). When compared to raw materials, TCLP results indicated that geopolymerization can significantly reduce the concentration of heavy metals in the medical waste ash leachate. The metal fixation percentages of the geopolymers ranged from 70 to 100%. The sequential extraction test results showed that geopolymerization (stabilization/solidification) is very beneficial in reducing the bioavailable fraction in the solid waste and maximizing the difficulty of fraction extraction.
engineering, civil, geological
What problem does this paper attempt to address?