Graphitic carbon nitride supported silver nanoparticles (AgNPs/g-C3N4): synthesis and photocatalytic behavior in the degradation of 2,4-dichlorophenoxyacetic acid
Phung Thi Lan,Nguyen Hoang Hao,Nguyen Trung Hieu,Nguyen Thi Thu Ha,C Trevor Brown,Le Minh Cam
DOI: https://doi.org/10.1039/d4ra02658f
2024-06-13
Abstract:Graphitic carbon nitride supported silver nanoparticles (AgNPs/g-C3N4) with 1%, 3%, and 5% AgNPs were successfully synthesized by an "ex situ" method with ultrasound of a mixture of AgNP solution and g-C3N4. The AgNP solution was prepared by chemical reduction with trisodium citrate, and g-C3N4 was synthesized from the urea precursor. The supported nanoparticles were characterized by X-ray diffraction spectroscopy (XRD), scanning electron microscopy (SEM), transmission electron microscopy (TEM), nitrogen adsorption-desorption (BET), Fourier transformation infrared (FTIR) and Raman spectroscopy, ultraviolet-visible diffuse reflectance spectroscopy (UV-Vis DRS), photoluminescence spectroscopy (PL), electron paramagnetic resonance (EPR) and electrochemical impedance spectroscopy (EIS) Nyquist plots. The visible light-driven photocurrent measurement was performed by three on-off cycles of intermittent irradiation. The analyses show that AgNPs were evenly dispersed on g-C3N4, and have sizes ranging from 40 to 50 nm. The optical properties of the AgNPs/g-C3N4 material were significantly enhanced due to the plasmonic effect of AgNPs. The photocatalytic activity of catalysts was evaluated by 2,4-D degradation under visible light irradiation (λ > 420 nm). In the reaction conditions: pH 2.2; C o (2,4-D) 40 ppm; a m/v ratio of 0.5 g L-1, AgNPs/g-C3N4 materials exhibit superior photocatalytic activity compared to the pristine g-C3N4. The studies on the influence of free radicals and photogenerated holes, h+, show that ˙OH, O2˙-, and h+ play decisive roles in the photocatalytic activity of AgNPs/g-C3N4. The TOC result indicates the minimal toxicity of the by-products formed during the 2,4-D degradation. In addition, the AgNPs/g-C3N4 catalytic activity under direct sunlight irradiation was similar to that under artificial UV irradiation. Based on these results, a possible mechanism is proposed to explain the enhanced photocatalytic activity and stability of AgNPs/g-C3N4. Theoretical calculations on the interaction between 2,4-D and g-C3N4, Ag/g-C3N4 was also performed. The calculated results show that the adsorption of 2,4-D on Ag-modified g-C3N4 is significantly more effective compared to pristine g-C3N4.