Abstract:2-Aminobenzenethiol (ABT) was first reported as a corrosion inhibitor for copper in sulfuric acid environment. The biggest bright spot in this work is the discovery that ABT as a corrosion inhibitor can show high-quality anti-corrosion feature at low concentrations (0.01 M–0.5 M). The polarization curve experiment data shows that the corrosion inhibition efficiency of ABT for Cu in 0.5 mol/L sulfuric acid environment is obviously more than 90%, and the corrosion inhibition efficiency is proportional to ABT concentration. Electrochemical impedance spectroscopy (EIS) experiment shows that the polarization resistance (Rp) in the blank solution is 0.38 kΩ cm2, and the Rp increased to 21.18 kΩ cm2 after adding 0.5 M ABT, and the corrosion inhibition efficiency is as high as 98.2%. The surface morphology test results show that the copper surface after adding ABT is significantly smoother than the copper surface in the blank solution. The X-ray photoelectron spectroscopy (XPS) experimental results show that the sulfur and nitrogen atoms in ABT can form coordination bonds with copper atoms, resulting in chemisorption. In addition, the adsorption isotherm model shows that the adsorption of ABT on the copper surface conforms to the Langmuir isotherm model. Quantum chemical (QC) calculations and molecular dynamics (MD) simulations have shown that ABT can show decent anti-corrosion feature.

Insight into the anti-corrosion mechanism of 2-aminobenzenethiol as the inhibitor for copper in acid environment