Abstract:In this paper, a series of CaMoO4 phosphor co-doped rare earth ions were prepared with chemistry co-precipitation method. The concentration of Pr(3+)/Tb(3+) and temperature had obvious influence on the luminescent properties. The crystal structures and spectrum characteristics of the samples were identified with X-ray powder diffraction (XRD) and fluorescence spectrophotometer (PL). According to XRD analysis, the main diffraction peaks of samples are consistent with the standard card (JCPDS 29-0351) of the diffraction peak data. This showed doped rare earth ions did not change matrix lattice structure. The emission spectrum excited by 275 nm exhibit sharp lines peaking at 488, 560, 621 and 560 nm assigned to the (3)P(0)—(3)H(4), (3)P(0)—(3)H(5)，(1)D(2)—(3)H(4) and (3)P(0)—(3)F(2) transitions of the Pr(3+) ions. The intensity of fluorescence reached the strongest when the concentration of the doping amount was 3%. The optimum calcination temperatures of CaMoO(4)∶0.03Pr(3+) and CaMoO(4)∶0.05Tb(3+) were 800 and 600 ℃. Furthermore, the intensity of excitation spectra and emission spectra are dependent on the concentration of the doping amount. The emission spectra intensities of CaMoO(4)∶Pr(3+) phosphors decrease and CaMoO(4)∶Tb(3+) phosphors firstly increase and then decrease because of concentration quenching effect with increasing Pr(3+) and Tb(3+) concentration. In addition, the luminescence properties of Pr(3+) ion in CaMoO(4)∶0.03Pr(3+), yTb(3+) system could be evidently improved with co-doping of Tb(3+) ions which was due to the efficient energy transfer process from Tb(3+) to Pr(3+) ions.

Room-temperature and ultra-fast Eu3+ ion doping for highly luminescent and extremely small CaMoO4 nanocrystals

An Ultrafast and Room‐Temperature Strategy for Kilogram‐Scale Synthesis of Sub‐5 nm Eu3+‐doped CaMO4 Nanocrystals with a Photoluminescence Quantum Yield Exceeding 85%

Low temperature synthesis and photoluminescent properties of CaMoO4:Eu3+ red phosphor with uniform micro-assemblies

Synthesis and Luminescence Behavior of Eu3+-doped CaF2 Nanoparticles

Enhancing Luminescence of Lu2MoO6:Eu3+ Phosphors by Doping with Li+ Ions for Near Ultraviolet Based Solid State Lighting

[Synthesis and Fluorescence Properties of Rare Earth Ions Co-Doped CaMoO(4)].

Luminescence Investigation of Eu~(3+)-Bi~(3+) Co-Doped CaMoO_4 Phosphor

White-light Emission and Weak Antiferromagnetism from Cubic Rare-Earth Oxide Eu2O3 Electrospun Nanostructures

Size-tailored synthesis and luminescent properties of three-dimensional BaMoO4 , BaMoO4 :Eu(3+) micron-octahedrons and micron-flowers via sonochemical route

Low-temperature in situ preparation of Eu3+/Tb3+-doped CaMoO4/SrMoO4 nanoparticle thin films and their application in anti-counterfeiting

Impact of luminescent-ion doping on the crystallographic and photo-physical properties of the CaMoO4 nanoparticles

A Novel Facile Room Temperature Chemical Lithiation for Reduction of Eu3+ in Nasicon Crystal Structure

Rapid synthesis of BaMoO4 :Eu3+ red phosphors using microwave irradiation

Nay(Moo4)(2) Microcrystals with Controlled Faceting and Their Tunable Photoluminescence Properties after Doping with Eu3+

Thermally Induced Morphological and Structural Transformations on Eu2+/Eu3+-Coactivated Calcium Silicate Nanophosphors

Lanthanide ions-doped SrMoO4 microcrystals: Synthesis, characterizations, luminescence, and detection of Fe3+ ions

Enhancement in Photoluminescence of CaMoO[sub 4]:Eu[sup 3+] Through Introducing MVO[sub 4] (M=Y or Bi)

Synthesis and real-time monitoring morphology evolution of luminescent Eu(TCPP) MOF

Solution-deposited and low temperature-annealed Eu3+/Tb3+-doped CaMoO4/SrMoO4 luminescent thin films

Microwave Synthesis of CaMoO 4 :Sm 3+ Orange Reddish-Emitting Phosphors and Its Photoluminescence Property

Ultrathin Ca-PO4-CO3 solid-solution nanowires: a controllable synthesis and full-color emission by rare-earth doping.