Influence of citric acid and sodium gluconate on hydration of calcium sulfoaluminate cement at various temperatures

Dinghua Zou,Zhenjie Zhang,Dongming Wang

DOI: https://doi.org/10.1016/j.conbuildmat.2020.120247

IF: 7.4

2020-12-01

Construction and Building Materials

Abstract:<p>To reveal the effect of set retarders on calcium sulfoaluminate (CSA) cement at different temperatures, plain paste and retarded ones with citric acid and sodium gluconate were prepared. Curing temperatures of 20, 30 and 40 °C were adopted. Initial and final setting times of fresh paste were measured. Compressive strength of samples at 1 day, and 3, 7, and 28 days were tested. XRD, DSC-TG and SEM were used to reveal the impact of retarders on hydration and microstructure of CSA cement. Results reveal that, retarders extend the setting of CSA cement paste, however accelerate the hydration of it at later age. Finer and more AFt is observed in retarded paste. Nevertheless, rise of temperature diminishes the retarding effect of citric acid and sodium gluconate and meanwhile inhibits the hydration of CSA cement with and without retarders. On most occasions, compressive strength of CSA cement paste increases when retarders are employed with the content up to 1.5%. At the content of 0.5 or 0.25%, retarded pastes achieve the highest compressive strength gains relative to their plain counterpart. This varies with the type of retarders and curing temperature. For citric acid and sodium gluconate, the contents are 0.25 and 0.5% at 20 °C, respectively. With the rise of temperature to 30 and 40 °C, the contents are 0.5 and 0.25%, respectively. Rise of temperature from 20 to 30 °C enhances the gain of compressive strength. However, similar gains are observed at temperatures of 30 and 40 °C.</p>

construction & building technology,materials science, multidisciplinary,engineering, civil