Multiphase Engineered BNT-Based Ceramics with Simultaneous High Polarization and Superior Breakdown Strength for Energy Storage Applications

Chaoqiong Zhu,Ziming Cai,Bingcheng Luo,Xu Cheng,Limin Guo,Ying Jiang,Xiuhua Cao,Zhenxiao Fu,Longtu Li,Xiaohui Wang
DOI: https://doi.org/10.1021/acsami.1c06075
2021-06-10
Abstract:Dielectric ceramics are crucial for high-temperature, pulse-power energy storage applications. However, the mutual restriction between the polarization and breakdown strength has been a significant challenge. Here, multiphase engineering controlled by the two-step sintering heating rate is adopted to simultaneously obtain a high polarization and breakdown strength in 0.8(0.95Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>–0.05SrZrO<sub>3</sub>)–0.2NaNbO<sub>3</sub> (BNTSZNN) ceramic systems. The coexistence of tetragonal (T) and rhombohedral (R) phases benefits the temperature stability of BNTSZNN ceramics. Increasing the heating rate during sintering reduces the diffusion of SrZrO<sub>3</sub> and NaNbO<sub>3</sub> into Bi<sub>0.5</sub>Na<sub>0.5</sub>TiO<sub>3</sub>, which results in a high proportion of the R phase and a finer grain size. The overall polarization is enhanced by increasing the proportion of the high-polarization R phase, which is demonstrated using a first-principles method. Meanwhile, the finer grain size enhances the breakdown strength. Following this design philosophy, an ultrahigh <i>W</i><sub>dis</sub> of 5.55 J/cm<sup>3</sup> and η above 85% is achieved in BNTSZNN ceramics as prepared with a fast heating rate of 60 °C/min given a simultaneously high polarization of 43 μC/cm<sup>2</sup> and high breakdown strength of 350 kV/cm. Variations in the discharge energy density from room temperature to 160 °C are less than 10%. Additionally, such BNTSZNN ceramics exhibit an ultrafast discharge speed with τ<sub>0.9</sub> at approximately 60 ns, which shows great potential in pulse-power system applications.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.1c06075?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.1c06075</a>.Weibull plots of the DC dielectric breakdown strength for BNTSZNN ceramics with various heating rates; unipolar hysteresis loops measured under each maximum applied electric field and at 1 Hz of the BNTSZNN ceramics sintered with various heating rates; pulsed discharge electric current–time (<i>I</i>–<i>t</i>) curves as a function of the applied electric field for the BNTSZNN-60 sample; TEM images and the SAED pattern of BNTSZNN-60 (<a class="ext-link" href="/doi/suppl/10.1021/acsami.1c06075/suppl_file/am1c06075_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
materials science, multidisciplinary,nanoscience & nanotechnology
What problem does this paper attempt to address?