Abstract:Platinum nanocrystals featuring a multiply twinned structure and uniform sizes below 5 nm are superb catalytic materials, but it is difficult to synthesize such particles owing to the high twin-boundary energy (166 mJ/m2) of Pt. Here, we report a simple route to the synthesis of such nanocrystals by selectively growing them from the vertices of Pd icosahedral seeds. The success of this synthesis critically depends on the introduction of Br– ions to slow the reduction kinetics of the Pt(II) precursor while limiting the surface diffusion of Pt adatoms by conducting the synthesis at 30 °C. Owing to the small size and multiply twinned structure of Pt dots, the as-obtained Pd–Pt nanocrystals show remarkably enhanced activity and durability toward oxygen reduction, with a mass activity of 1.23 A mg–1Pt and a specific activity of 0.99 mA cm–2Pt, which are 8.2 and 4.5 times as high as those of the commercial Pt/C.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acs.nanolett.1c00007?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acs.nanolett.1c00007</a>.Synthetic protocols; TEM image of the Pd icosahedral seeds; size distribution of Pt dots; time-elapsed TEM images of Pd–Pt great icosahedra; TEM images of Pd–Pt nanocrystals synthesized with different amounts of K2PtCl4, without Br–, or at a higher temperature; and CV and ORR polarization curves recorded from the commercial Pt/C catalyst before and after different cycles of ADT (<a class="ext-link" href="/doi/suppl/10.1021/acs.nanolett.1c00007/suppl_file/nl1c00007_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

High yield synthesis of catalytically active five-fold twinned Pt nanorods from a surfactant-ligated precursor

Short peptide-directed synthesis of one-dimensional platinum nanostructures with controllable morphologies

Epitaxial Growth of Twinned Au-Pt Core-Shell Star-Shaped Decahedra As Highly Durable Electrocatalysts.

One-pot Synthesis of PtRu Nanodendrites As Efficient Catalysts for Methanol Oxidation Reaction.

Surfactant-Guided Synthesis of Porous Pt Shells with Ordered Tangential Channels, Coated on Pd Nanostructures, and Their Enhanced Catalytic Activities.

Engineering Porosity into Trimetallic PtPdNi Nanospheres for Enhanced Electrocatalytic Oxygen Reduction Activity

Ph-Dependent Growth of Atomic Pd Layers on Trisoctahedral Gold Nanoparticles to Realize Enhanced Performance in Electrocatalysis and Chemical Catalysis

Facile Synthesis of Porous Dendritic Bimetallic Platinum-Nickel Nanocrystals As Efficient Catalysts for the Oxygen Reduction Reaction

Synthesis, Purification, and Electrocatalytic Activity of Platinum Nanocatalyst with Globular Dendritic Structure

Twin-Directed Deposition of Pt on Pd Icosahedral Nanocrystals for Catalysts with Enhanced Activity and Durability toward Oxygen Reduction

Ultrathin and Ultralong Single-Crystal Platinum Nanowire Assemblies with Highly Stable Electrocatalytic Activity.

Ultrathin And Ultralong Single-Crystal Platinum Nanowire Assemblies With Highly Stable Electrocatalytic Activity

Freestanding Penta‐Twinned Palladium Nanosheets

Five‐Fold Twinned Pd Nanorods and Their Use As Templates for the Synthesis of Bimetallic or Hollow Nanostructures

Atomically Dispersed Pt On Screw-Like Pd/Au Core-Shell Nanowires For Enhanced Electrocatalysis

Etching suppression as a means to Pt dendritic ultrathin nanosheets by seeded growth

Freestanding Penta-Twinned Pd-Ag Nanosheets

Shape-Selective Synthesis and Facet-Dependent Enhanced Electrocatalytic Activity and Durability of Monodisperse Sub-10 Nm Pt-Pd Tetrahedrons and Cubes

One-Pot Synthesis of Ultra-Small Pt Nanoparticles-Loaded Nitrogen-Doped Mesoporous Carbon Nanotube for Efficient Catalytic Reaction

Solvothermal Synthesis of Nanostructured PtnNi Tetrahedrons with Enhanced Platinum Utilization and Activity Toward Oxygen Reduction Electrocatalysis

Shape-controlled synthesis of platinum nanocrystals for catalytic and electrocatalytic applications