Abstract:Introduction: Hydroxyapatite (HA) is the principal inorganic constituent of human bone. Due to its good biocompatibility and osteoconductivity, all kinds of HA particles were prepared by different methods. Numerous reports demonstrated that the properties of HA affected its biological effects. Methods: Two kinds of nanohydroxyapatite with different sizes and crystallinities were obtained via a hydrothermal treatment method under different temperatures. It was found that at a temperature of 140 C, a rod-like crystal (n-HA1) with a diameter of 23 +/- 5 nm, a length of 47 +/- 14 nm, and crystallinity of 85% +/- 5% was produced, while at a temperature of 80 degrees C, a -rod-like crystal (n-HA2) with a diameter of 16 +/- 3 nm, a length of 40 +/- 10 nm, and -crystallinity of 65% +/- 3% was produced. The influence of nanohydroxyapatite size and crystallinity on osteoblast viability was studied by MTT, scanning electron microscopy, and flow cytometry. Results: n-HA1 gave a better biological response than n-HA2 in promoting cell growth and inhibiting cell apoptosis, and also exhibited much more active cell morphology. Alkaline phosphatase activity for both n-HA2 and n-HA1 was obviously higher than for the control, and no significant difference was found between n-HA1 and n-HA2. The same trend was observed on Western blotting for expression of type I collagen and osteopontin. In addition, it was found by transmission electron microscopy that large quantities of n-HA2 entered into the cell and damaged the cellular morphology. Release of tumor necrosis factor alpha from n-HA2 was markedly higher than from n-HA1, indicating that n-HA2 might trigger a severe inflammatory response. Conclusion: This work indicates that not all nanohydroxyapatite should be considered a good biomaterial in future clinical applications.

Investigation on [OH − ]-responsive systems for construction of one-dimensional hydroxyapatite via a solvothermal method

“Cleaning” the surface of hydroxyapatite nanorods by a reaction-dissolution approach

Hydrothermal synthesis of nano-hydroxyapatite crystals

Influence of Solvothermal Reaction Temperature on Hydroxyapatite Nanowires

Investigation of various fatty acid surfactants on the microstructure of flexible hydroxyapatite nanofibers

Nucleation and growth of hydroxyapatite nanocrystals by hydrothermal method

Controlled Synthesis of Hydroxyapatite Nanomaterials Regulated by Different Phosphorus Sources

Controllable preparation of ultralong hydroxyapatite nanofibers using the solvothermal method: Effect of initial Ca/P ratios

Effect of NaOH Concentration on Formation of Ba4Ti13O30 and BaTi5O11 Nanocrystals Prepared by Hydrothermal Method

Hydrothermal Synthesis of Hydroxyapatite Whisker

Synthesis and size evolution of 1D hydroxyapatite crystals under surfactant-free hydrothermal conditions

Cell responses to two kinds of nanohydroxyapatite with different sizes and crystallinities.

Solvothermal Synthesis of Hydroxyapatite Nanorods with Assistance of Green Polymer.

The influence of pH and temperature on the morphology of hydroxyapatite synthesized by hydrothermal method

Investigation of EDTA concentration on the size of carbonated flowerlike hydroxyapatite microspheres

Preparation and Characterization of Hydroxyapatite Nanotubes

Initial solution pH value for the construction of a 3D hydroxyapatite via the trisodium citrate-assisted hydrothermal route

The Preparation of Hydroxyapatite Nanowires and Nanorods Via Aliphatic Micelles As Soft Templates

Preparation and characterization of hydroxyapatite suspensions for solid freeform fabrication

Manipulation of partially oriented hydroxyapatite building blocks to form flowerlike bundles without acid-base regulation

The effects of graded doses of a cholecystokinin-like peptide with and without secretin on pancreatic growth and synthesis of RNA and polyamines in rats.