Three-Dimensional Bioprinting of Strontium-Modified Controlled Assembly of Collagen Polylactic Acid Composite Scaffold for Bone Repair

Weiwei Sun,Wenyu Xie,Kun Hu,Zongwen Yang,Lu Han,Luhai Li,Yuansheng Qi,Yen Wei

DOI: https://doi.org/10.3390/polym16040498

IF: 5

2024-02-11

Polymers

Abstract:In recent years, the incidence of bone defects has been increasing year by year. Bone transplantation has become the most needed surgery after a blood transfusion and shows a rising trend. Three-dimensional-printed implants can be arbitrarily shaped according to the defects of tissues and organs to achieve perfect morphological repair, opening a new way for non-traumatic repair and functional reconstruction. In this paper, strontium-doped mineralized collagen was first prepared by an in vitro biomimetic mineralization method and then polylactic acid was homogeneously blended with the mineralized collagen to produce a comprehensive bone repair scaffold by a gas extrusion 3D printing method. Characterization through scanning electron microscopy, X-ray diffraction, and mechanical testing revealed that the strontium-functionalized composite scaffold exhibits an inorganic composition and nanostructure akin to those of human bone tissue. The scaffold possesses uniformly distributed and interconnected pores, with a compressive strength reaching 21.04 MPa. The strontium doping in the mineralized collagen improved the biocompatibility of the scaffold and inhibited the differentiation of osteoclasts to promote bone regeneration. This innovative composite scaffold holds significant promise in the field of bone tissue engineering, providing a forward-thinking solution for prospective bone injury repair.

polymer science

What problem does this paper attempt to address?

The paper attempts to address the development and optimization of materials for bone defect repair. Specifically, the researchers prepared a strontium ion-containing collagen-polylactic acid (PLA) composite scaffold using three-dimensional bioprinting technology, aiming to enhance the biocompatibility and bone regeneration capability of the scaffold to achieve better bone defect repair outcomes.

### Main Issues:
1. **Challenges in Bone Defect Repair**:
- Although bone graft surgeries are common, they are not effective for repairing large-area bone defects.
- Three-dimensional scaffolds made from single biomaterials have drawbacks such as poor bioactivity, insufficient mechanical properties, and lack of osteoinductive effects.

2. **Limitations of Existing Materials**:
- Common bone repair methods rely on the self-repair ability of the fracture or bone defect site, but this approach is limited in treating large-area bone defects.
- Three-dimensional scaffolds made from single materials struggle to meet the comprehensive requirements of structural support, mechanical properties, and bioactivity needed for bone tissue engineering.

### Solutions:
1. **Preparation of Strontium-Doped Mineralized Collagen**:
- Strontium-doped mineralized collagen (SrMC) was prepared using an in vitro biomimetic mineralization method and uniformly mixed with PLA to create a composite scaffold.
- The incorporation of strontium ions improved the biocompatibility of the scaffold and inhibited the differentiation of osteoclasts, thereby promoting bone regeneration.

2. **Application of 3D Bioprinting Technology**:
- 3D printing technology was used to prepare composite scaffolds with specific pore sizes and interconnected pore structures, ensuring the mechanical properties and bioactivity of the scaffold.
- Printing parameters were optimized to avoid the adverse effects of high temperatures on PLA materials while ensuring a high content of mineralized collagen.

### Research Significance:
- **Biocompatibility and Mechanical Properties**: The strontium-doped composite scaffold exhibited inorganic components and nanostructures similar to human bone tissue, with uniformly distributed interconnected pores and a compressive strength of 21.04 MPa.
- **Bone Regeneration Capability**: The incorporation of strontium ions significantly improved the biocompatibility of the scaffold, inhibited the differentiation of osteoclasts, and promoted bone regeneration.
- **Application Prospects**: This innovative composite scaffold has significant application prospects in the field of bone tissue engineering, providing new ideas for future bone injury repair.

In summary, this paper addresses some key issues in bone defect repair by preparing and characterizing a strontium-doped collagen-PLA composite scaffold, offering new solutions for the development of bone tissue engineering.