Advancing energy storage capabilities in 0.7BNST(1-)-0.3BLMN lead-free dielectric ceramic materials

Guangzhi Dong,Yaming Jin,Xiaorong Yang,Luyao Wang,Yifan Zhang,Yi Quan,Chunlong Fei,Tianlong Zhao,Yang Liu,Rusen Yang,Biaolin Peng,Huiqing Fan

DOI: https://doi.org/10.1016/j.ceramint.2024.03.057

IF: 5.532

2024-03-01

Ceramics International

Abstract:Lead-free ferroelectric ceramics with a composition of 0.7(Bi0.5Na0.5)0.7Sr0.3Ti(1-x)O3-0.3Ba0.94La0.04(Mg1/3Nb2/3) x O3 (abbreviated as 0.7BNST(1-x)-0.3BL(MN) x , 0 ≤ x ≤ 0.12) were prepared using solid-phase sintering method, involving co-substituting at A and B sites. High recoverable energy density (W rec) of 3.54 J/cm3 and energy efficiency (η) 85.49% are achieved at an electric field of 270 kV/cm. Furthermore, these ceramics exhibited excellent temperature and cycle stability at 120 kV/cm (within 25 °C–150 °C, W rec fluctuation range <14 %; under 1∼106 cycles, the W rec fluctuation range <5 %). In terms of dielectric performance, they exhibited a high dielectric constant (ε r∼4540), an extremely low dielectric loss tanδ of <0.04 (30 °C–300 °C), and good temperature stability with Δε/ε 150 °C ≤ ±15 % (−19.5 °C–233.4 °C). During the charging and discharging process, these ceramics demonstrated a high energy density (W d) of 1.2 J/cm3, a power density (P D) of 61.7 MW/cm3, and an extremely short discharge time (t 0.9) of approximately ∼0.11 μs＀ This study has improved the dielectric energy storage performance of BNT-based lead-free piezoelectric ceramics, making them suitable for use in pulse power devices.

materials science, ceramics