Thickness and Humidity on Proton Conductivity in MOF-508 Thin Film by Twin-Zinc-Source Method

Kun Zhang,Chunxia Wang,Feng Yang,Jing Li,Shuguang Yan,Yue Qi

DOI: https://doi.org/10.3390/coatings13091520

IF: 3.236

2023-08-30

Coatings

Abstract:To achieve structurally stable and high proton conductive materials, preferably under ambient humidity and pressure, the well-controlled thickness and conductivity of the MOF thin films represent an effective approach. Electrodes are the most important part of fuel cells; proton conducting materials are often used for electrodes, but today high proton conducting materials are expensive and use harsh conditions. Therefore, the goal of researchers is the pursuit of stable structure high proton conductive materials. We prepared well controlled thickness and conductive MOF-508a thin films on a Zn substrate by the "twin zinc source" method, which is very rare in conventional proton conductive materials. The results show that when the thickness of the MOF-508a/Zn thin film was at its minimum (16 μm), the resistivity and proton conductivity reached 2.5 × 103 Ω cm and 4 × 10−4 S cm−1, respectively. The MOF-508b/Zn thin film can absorb water molecules in a high humidity atmosphere and the conductivity decreases significantly with increasing humidity. When the film was put into the atmosphere with a relative humidity of 85%, the resistivity reached 200 Ω cm significantly. This work provides a simple, low cost, and environmentally friendly strategy for fabricating high proton conducting MOF films by exploring the "twin-zinc-source" method, which is critically important for PEMFC. It is believed that higher conductivity MOF films can be obtained with further modifications, indicating the potential of such films as humidity detectors.

materials science, multidisciplinary,physics, applied, coatings & films

What problem does this paper attempt to address?

### Problems Addressed by the Paper

This paper aims to address the application of metal-organic framework (MOF) films in fuel cells, particularly in the area of proton-conducting materials. Specifically, the researchers' goal is to develop materials that are structurally stable and have high proton conductivity, ideally functioning under ambient humidity and pressure.

#### Main Research Content:
1. **Dual Zinc Source Method**: The MOF-508a film was prepared using the "dual zinc source" method, and the effects of film thickness and humidity on its proton conductivity were studied.
2. **Film Thickness Control**: It was found that the film thickness can be controlled by adjusting the reaction time and the concentration of zinc ions (Zn2+).
3. **Proton Conductivity Testing**: The resistivity and proton conductivity of MOF-508a films of different thicknesses were tested using AC impedance measurements.
4. **Humidity Impact**: The performance of the film under different humidity conditions was studied, revealing that increased humidity leads to a significant decrease in conductivity.

#### Conclusion:
- When the MOF-508a film thickness is 16 micrometers, its resistivity is 2.5 × 10^3 Ω·cm, and its proton conductivity is 4 × 10^−4 S·cm^−1.
- In a high humidity environment (relative humidity 85%), the film's resistivity significantly rises to 200 Ω·cm.
- The study proposes a simple, low-cost, and environmentally friendly method to prepare high proton-conducting MOF films, providing a new strategy for the application of proton exchange membrane fuel cells (PEMFC).
- With further improvements, this type of film could potentially be used as a humidity detector in the future.