A systematic study on gelatinization efficiency of starch by NaOH for enhanced hematite depression
Elaine Cristina Andrade,Saeed Chehreh Chelgani,Laurindo de Salles Leal Filho
DOI: https://doi.org/10.1016/j.mineng.2024.108621
IF: 5.479
2024-02-17
Minerals Engineering
Abstract:Starch is a traditional depressant for hematite beneficiation by cationic reverse flotation separation from silicates. Alkali or thermal gelatinization must be used to prepare starch and promote its dissolution in water. In industry, gelatinization is typically carried out using sodium hydroxide at room temperature at different starch/NaOH mass ratios (SNMR). Surprisingly, no investigation has systematically studied the optimum SNMR for boosting hematite depression. This work examined the influence of starch gelatinization under various SNMR (3:1, 5:1, 7:1, and 9:1) on hematite depression (at pH = 10.5, 22 °C) by exploring flotation response ( R ), contact angle ( θ ), induction time ( τ ), hydrodynamic diameter ( d H ) of starch macromolecules, total energy of interaction starch/hematite (G TOT ), based on its two components: the attractive Lifshitz-van der Waals energy (G LW ) and attractive/repulsive electrostatic energy (G EL ). Flotation test results indicated that SNMR = 5:1 promoted the lowest hematite recovery (14.8 %), coupled with the highest induction time ( τ = 55 ms) and the lowest contact angle ( θ = 11°). The hydrodynamic diameter ( d H ) of macromolecules in solutions prepared under different SNMR was determined by Dynamic Light Scattering, showing three peaks: amylopectin (350 < d H < 420 nm), amylose (50 < d H < 100 nm) and debris from gelatinization ( d H ∼ 5000 nm). Since the latter only occurred in solutions prepared under SNMR of 7:1 and 9:1, deficient hematite depression might be caused by incomplete gelatinization. As amylopectin is the starch component that is responsible for its depressant ability, larger amylopectin macromolecules ( d H = 411 nm) found in solutions prepared at SNMR = 5:1 contrast with smaller macromolecules ( d H = 353 nm) produced at SNMR = 3:1. Considering starch macromolecules as a sphere, and hematite's surface as a plane; G LW , G EL , and G TOT were calculated in function of the sphere/plane separation distance (2 nm < H < 20 nm). G LW was determined based on the assessment of the Hamaker constant of the starch/water/hematite system (2.9 × 10 −20 J < A 132 < 3.3 × 10 −20 J), whereas G EL was determined based on the zeta potential of starch (−2mV < ζ1 < −4mV) and hematite ( ζ2 = −29 mV). G TOT for starch gelatinized at SNMR = 5:1 (−502.9 × 10 −21 J) is greater than G TOT for starch prepared at SNMR = 3:1 (−468.8 × 10 −21 J) and SNMR = 7:1 (−469.0 × 10 −21 J), at a confidence level of 95 %. These results corroborate the more intensive hematite depression by starch prepared at SNMR = 5:1 compared to the other values explored by this study.
engineering, chemical,mining & mineral processing,mineralogy