Numerical Optimization and Performance Study of Ni-Based Coatings on Gray Cast Iron Surface by High-Speed Laser Cladding Based on Orthogonal Test
Huan Li,Muhua Mao,Rui Wang,Runze Wei,Chunjiang Zhao,Changyao Ouyang,Rui Deng,Qiaofeng Bai
DOI: https://doi.org/10.1007/s11665-024-09487-3
IF: 2.3
2024-05-02
Journal of Materials Engineering and Performance
Abstract:To improve the cladding quality of Ni-based powder on gray cast iron by high-speed laser cladding, ANSYS was used to construct the cladding model. The effects of laser power P , scanning rate v , and spot diameter r on the cladding quality were explored in terms of substrate surface temperature, temperature gradient G /solidification rate R , and heat-affected zone (HAZ) by the three-factor and three-level orthogonal test. The parameters that significantly affect the factors v and r were determined. Based on simulation tests, the effect of P on the microstructure, hardness and wear resistance of the molten layer was investigated by using scanning electron microscopy (SEM), hardness tester, friction wear machine and ultra-depth of field. The results showed that the microstructure of the cladding layer became sparse and coarse with increasing P , and the cross-sectional hardness and surface hardness didn't change much. Compared to 2000 W, the wear quality loss of 1600 and 2400 W is improved by 24.8, 40.4%. The best wear resistance was achieved for 2000 W. The wear resistance and bond strength of Ni-based coating are optimal when v = 3 mm, r = 30 mm/s, and P = 2000 W.
materials science, multidisciplinary