Abstract:We have systematically investigated the annealing effect on the superconductivity of iron chalcogenide Fe1+y(Te1-xSex). The atmospheres used for annealing include O2, N2, I2 vapor, air and vacuum. We observed that annealing in O2, I2 and air could enhance superconductivity for the underdoped samples, consistent with the results reported in literatures. Interestingly, we found that annealing in N2 also leads to superconductivity enhancement, similar to the annealing effects of O2, I2 and air. However, vacuum annealing does not enhance superconductivity, which indicates that the enhanced superconductivity in O2-, N2-, I2- and air-annealed samples is not due to improved homogeneity. In addition, we have treated the underdoped samples with nitric acid, which is found to enhance superconductivity as well. Our analyses of these results support the argument that the superconductivity enhancement, caused either by annealing or nitric acid treatment, originates from the variation of interstitial Fe. The interstitial Fe, which is destructive to superconducting pairing, can be reduced by annealing in oxidation agents or nitric acid treatment. We also find that although N2-, O2- and air-annealed samples exhibit strong superconducting diamagnetism with -4pichi ~1 (chi, dc magnetic susceptibility) for some samples, their actual superconducting volume fraction probed by specific heat is low, ranging from 10% to 30% for 0.09 < x < 0.3, indicating that the superconductivity suppression remains significant even in annealed samples. The strong diamagnetism is associated with the superconducting shielding effect on the non-superconducting phase. We have also established the phase diagram of the annealed samples and compared it with that of the as-grown samples. The effect of annealing on the interplay between magnetism and superconductivity is discussed.

Superconductivity in Fe1+dTe0.9Se0.1 induced by deintercalation of excess Fe using alcoholic beverage treatment

Clarification as to why alcoholic beverages have the ability to induce superconductivity in Fe_{1+d}Te_{1-x}S_x

Alcoholic beverages induce superconductivity in FeTe$_{1-x}$S$_x$

Annealing, acid, and alcoholic beverage effects on Fe1+yTe0.6Se0.4

Tartaric acid in red wine as one of the key factors to induce superconductivity in FeTe0.8S0.2

Bulk Superconductivity in Fe1+yTe0.6Se0.4 Induced by Removal of Excess Fe

Phase Diagram and Annealing Effect for Fe1+δTe1−xSxsingle Crystals

Interstitial Iron Controlled Superconductivity in Fe1+xTe0.7Se0.3

Study of Composition-Modulated Interband Transitions Characteristic and Charge Dynamics Response of High-Throughput Fese1-Xtex Combinatorial Film

EXTRA OXYGEN DEFECT INDUCED BY Fe-DOPING IN Tl-SYSTEM SUPERCONDUCTOR

Probing the Direct Factor for Superconductivity in FeSe-Based Superconductors by Raman Scattering

Inhomogeneous superconductivity induced by interstitial Fe deintercalation in oxidizing-agent-annealed and HNO3-treated Fe1+y(Te1-xSex)

Effects of Te- and Fe-doping on the Superconducting Properties in FeySe1-xTex Thin Films

Evolution of Superconductivity in Fe$_{1+y}$Te$_{1-x}$Se$_{x}$ Annealed in Te Vapor

Resurgence of superconductivity and the role of $d_{xy}$ hole band in FeSe$_{1-x}$Te$_x$

Magnetic and Superconducting Properties in Single Crystalline Fe1+δTe1-xSex (x<0.50) System

Influence of interstitial Fe to the phase diagram of Fe$_{1+y}$Te$_{1-x}$Se$_x$ single crystals

Enhancement of Superconductivity in FeSe 0.5 Te 0.5 by Furnace Cooling

Protonation-induced discrete superconducting phases in bulk FeSe single crystals

Improving Superconducting Performance of Fe(Se, Te) with In Situ Formed Grain-Boundary Strengthening and Flux Pinning Centers

Effect of annealing on superconductivity in Fe 1+ y (Te 1− x S x ) system