Influence of phase transition with annealing temperature on structural, morphological, and supercapacitive characteristics of molybdenum oxide nanostructures

Meenal D. Patil,Umesh V. Shembade,Rhishikesh A. Moholkar,Suhas R. Ghatage,Annasaheb V. Moholkar
DOI: https://doi.org/10.1016/j.colsurfa.2024.134228
IF: 5.518
2024-05-23
Colloids and Surfaces A Physicochemical and Engineering Aspects
Abstract:In this study, molybdenum oxide nanostructures (MoO 3 NSs) were effectively synthesized through a simple, low-cost, surfactant-free, low-temperature, and scalable chemical co-precipitation method and investigated their synergistic effect with annealing temperature on energy storage applications for the first time. Herein, we have reported a phase transition of MoO 3 NSs from hexagonal to orthorhombic after the annealing temperature varied from 100°C to 500°C at constant time. Additionally, the resultant NSs were thoroughly examined for their physio-chemical characteristics, which revealed the stable phase formation of the MoO 3 NSs, respectively. Furthermore, the electroactive MoO 3 NSs were pasted on Ni-foam substrate (M@NF), and electrochemical properties were evaluated using a three-electrode setup at room-air temperature in 1 M KOH aqueous electrolyte across the potential range of 0 V to 0.786 V. As a result, the M@NF-5 electrode exhibited an impressive specific capacitance of 976.84 F g −1 at a scan rate of 1 mV s −1 , a higher energy density of 73.69 Wh kg −1 , and a power density of 655 W kg −1 at 5 mA g −1 The non-linear galvanostatic charge-discharge (GCD) profile aligns well with the cyclic voltammetry (CV) analysis. Both CV and GCD techniques confirm the pseudocapacitive behavior, with 83% capacitive retention observed after 2000 cycles. The fabricated symmetric device (M@NF-5//M@NF-5) exhibits enhanced electrochemical performance with a specific capacitance of 67.35 F g −1 at 5 mA g −1 and with an energy density of 18 Wh kg −1 , and a power density of 1750 W kg −1 at a specific current. These findings underscore the potential of chemically deposited α-MoO 3 as an auspicious material for use in supercapacitor applications.
chemistry, physical
What problem does this paper attempt to address?