Boosting the Zn-storage performance of layered VSe 2 cathodes via an in situ electrochemical oxidation strategy

Weiwei Wang,Ling Ran,Ruiting Hu,Chi Zhang,Rui Huang,Yani Li,Yao Ouyang,Jun Yan

DOI: https://doi.org/10.1016/j.jallcom.2024.173692

IF: 6.2

2024-02-02

Journal of Alloys and Compounds

Abstract:Layered VSe 2 with high electronic conductivity, low ion migration barriers and large interlayer spacing is a potential cathode material for Zn-ion batteries (ZIBs). However, relying only on the V 3+ /V 4+ redox pair, VSe 2 exhibits unsatisfactory Zn-storage performance. Considering the multiple electron transfer of V atoms, it is expected that the specific capacity will be enhanced by raising V 4+ to V 5+ . In this light, a simple in-situ electrochemical oxidation strategy was used to raise the valence state of V atoms in VSe 2 to boost its Zn-storage performance. Experimental results and material characterization indicate that the initial VSe 2 cathode undergoes an in-situ electrochemical oxidation-induced irreversible phase transformation process from VSe 2 to amorphous V 2 O 5 at a high potential (1.35–1.8 V vs. Zn/Zn 2+ ) during the first charge. In the subsequent cycles, the resulting amorphous V 2 O 5 cathode with high valence state and abundant active sites become the new host for Zn-storage, it can deliver a high specific capacity of 302.5 mAh g −1 at 0.1 A g −1 (3 times higher than that of the initial VSe 2 cathode), a satisfactory rate performance of 116.1 mAh g −1 at 2 A g −1 , and a long cycle life of 4000 cycles at 2 A g −1 . This work not only investigates the electrochemical oxidation mechanism of the VSe 2 cathode, but also provides a new insight into the design of high-performance cathode materials for large voltage ranges.

materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering