Two-stage cyclic ammonium sulfate roasting and leaching of extracting vanadium and titanium from vanadium slag

Qing Lin,Guoquan Zhang,Kun Wang,Dongmei Luo,Siyang Tang,Hairong Yue

DOI: https://doi.org/10.1016/j.cjche.2021.05.035

IF: 3.8

2021-07-01

Chinese Journal of Chemical Engineering

Abstract:Compared with traditional sodium or calcification roasting process for vanadium extraction from raw vanadium slag(V-slag), ammonium sulfate (AS) roasting could reduce about 470 °C roasting temperature and avoid Cl2, HCl, sodium-containing waste-water and waste gypsum discharging. To reduce the amount of AS added in vanadium extraction process, an efficient AS two-stage cyclic roasting and acid leaching process was proposed. The result of TG analysis indicates V- slag could be decomposed in 275-380 °C using AS roasting process. Using 2.03:1 total mass ratio of AS to V-slag, 90.86% V and 80.54% Ti could be extracted after 380℃ roasting for 30 min and 8% initial concentration of H2SO4 leaching at 70 ℃ for 100 min. XRD analysis indicates V-containing spinel phase in the 1st stage leaching residue would be efficiently decomposed by the cyclic two-stage roasting and leaching process. Furthermore, the valence of V(III) in raw V-slag was not changed after the 1st AS roasting stage, but a part of V(III) in the 1st leaching residue was oxidized to V(V) after 2nd roasting process.

engineering, chemical