Tall oil fatty acid-based alkyd-acrylic copolymers: Synthesis, characterization, and utilization in surface coating applications

Pirita Rämänen

2014-11-28

Abstract:Due to increased awareness of environmental issues and tightened legislation, bio-based substitutes for traditional petroleum-based polymers are being increasingly sought. Tall oil fatty acid (TOFA) is an attractive material for that purpose being a by-product of kraft pulping. Thus, it is abundant year-round, the price is reasonable, and it does not compete with foodstuff materials. In this study, the preparation and properties of TOFA-based waterborne materials for various coating and barrier applications were examined. Alkyd-acrylic copolymers were synthesized from conjugated and nonconjugated fatty acid-based alkyd resins, as well from rapeseed oil-based alkyd resins for comparison. The polymerization was performed in a miniemulsion, because of the stability and copolymer formation issues. The ratio between the alkyd resin and acrylate monomers was varied and the effect on copolymerization and the copolymer binder properties, such as monomer conversion and grafting of acrylate to the alkyd resin was studied. It was observed that the monomers butyl acrylate (BA) and methyl methacrylate (MMA) showed dissimilar affinity for the grafting site. The steric hindrances prevented MMA from reacting with the double bonds of the fatty acids as readily as BA. The allylic, especially the bis-allylic sites, were the principal grafting sites of MMA, for energetic reasons. However, this effectively retarded the polymerization and increased the homopolymerization of the acrylates. Limiting monomer conversion was overcome, using post-initiation. This research showed that it is possible to prepare stable dispersions of TOFA-based alkyd-acrylate copolymers with varied chemical composition. Self-standing films of these dispersions can be prepared and the dispersions applied effortlessly on paperboard and utilized as barrier material. An increased amount of alkyd resin made the copolymer films more brittle and increased their hydrophobicity. Oxygen barrier performance of the materials was not adequate, but was improved with cellulose. Various cellulose types were modified with TOFA to improve the compatibility between cellulose and polymer matrix. Modified cellulose was added to the copolymer dispersion to improve the mechanical and barrier performance of the copolymer films and coatings. Enhanced strength as well as increased oxygen barrier properties were clearly observed when cellulose was used as filler. The water barrier of the coatings was favorable despite the material composition.%%%%Biopohjaisten materiaalien hyodyntaminen erilaisissa sovelluksissa on tullut yha suositummaksi lisaantyneen ymparistotietoisuuden myota. Lisaksi raakaoljyn epavakaat maailmanmarkkinat ovat edesauttaneet biopohjaisten korvaajien etsintaa synteettisille, raakaoljysta valmistetuille materiaaleille. Tutkittuja ja kaytettyja yhdisteita ovat erilaiset kasvioljyt, kuten soijapapuoljy, rapsioljy ja auringonkukkaoljy. Mantyoljyn hyodyntaminen on vahaisempaa sen suppeamman esiintymisalueen vuoksi. Mantyoljya saadaan sellukeiton sivutuotteena, joten se on…

Materials Science,Environmental Science