Hydrophobic Electrode Design for CO 2 Electroreduction in a Microchannel Reactor

Jing Lin,Shenglin Yan,Chunxiao Zhang,Qing Hu,Zhenmin Cheng

DOI: https://doi.org/10.1021/acsami.1c23744

2022-02-02

Abstract:Microchannel reactor is a novel electrochemical device to intensify CO₂ mass transfer with large interfacial areas. However, if the catalyst inserted in the microchannel is wetted, CO₂ is required to diffuse across the liquid film to get access to reaction sites. In this paper, a hydrophobic polytetrafluoroethylene (PTFE)-doped Ag nanocatalyst on a Zn rod was synthesized through a facile galvanic replacement of 2Ag⁺+Zn → 2Ag + Zn²⁺. The catalyst layer, which was PTFE incorporated into the Ag matrix, was detected to distribute uniformly on the Zn substrate with a thickness of 77 μm. Consequently, the PTFE-doped electrode demonstrated enhanced activity with an optimal 96.19% CO faradaic efficiency (FE_CO) in the microchannel reactor. Typically, the catalyst could maintain over 90% FE_CO even at the current density of 24 mA cm^-2, which was nearly 30% higher than that of a similar catalyst without PTFE. In addition, influences of the concentration of PTFE and deposition time were also investigated, determining that 1 vol % of PTFE and 30 min of coating yielded best electrocatalytic efficiency. To achieve a further breakthrough of CO₂ mass transfer limitations, reactions were applied under relatively high pressures (3-15 bar) in a single-compartment high-pressure cell. The maximum CO partial current density (<i>j</i>_CO) can reach 106.76 mA cm^-2 at 9 bar.

materials science, multidisciplinary,nanoscience & nanotechnology