Abstract:A simple and environmentally friendly approach toward the thermoplastic processing of rapidly degradable plastic-enzyme composites using three-dimensional (3D) printing techniques is described. Polycaprolactone/Amano lipase (PCL/AL) composite films (10 mm × 10 mm; height [h] = ∼400 μm) with an AL loading of 0.1, 1.0, and 5.0% were prepared via 3D printing techniques that entail direct mixing in the solid state and thermal layer-by-layer extrusion. It was found that AL can tolerate in situ processing temperatures up to 130 °C in the solid-state for 60 min without loss of enzymatic activity. The composites were degraded in phosphate buffer (8 mg/mL, composite to buffer) for 7 days at 37 °C and the resulting average percent total weight loss (WLavg %) was found to be 5.2, 92.9, and 100%, for the 0.1, 1.0, and 5.0% films, respectively. The degradation rates of PCL/AL composites were found to be faster than AL applied externally in the buffer. Thicker PCL/AL 1.0% films (10 mm × 10 mm; h = ∼500 μm) were also degraded over a 7 day period to examine how the weight loss occurs over time with 3.0, 18.1, 36.4, 46.4, and 70.2% weight loss for days 1, 2, 3, 4, and 7, respectively. Differential scanning calorimetry (DSC) analysis shows that the film's percent crystallinity (Dxtal%) increases over time with Dxtal% = 46.5 for day 0 and 53.1% for day 7. Scanning electron microscopy (SEM) analysis found that film erosion begins at the surface and that water can penetrate the interior via surface pores activating the enzymes embedded in the film. Controlled release experiments utilizing dye-loaded PCL/AL/dye (AL = 1.0%; dye = 0.1%) composites were degraded over a 7 day period with the bulk of the dye released by the fourth day. The PCL/AL multimaterial objects containing AL-resistant polylactic acid (PLA) were also printed and degraded to demonstrate the application of this material on more complex structures.

Directed Evolution of Material Binding Peptide for Polylactic Acid-specific Degradation in Mixed Plastic Wastes

New insights into the biodegradation of polylactic acid: from degradation to upcycling

Computational Design of an Efficient and Thermostable Esterase for Polylactic Acid Depolymerization

An engineered enzyme embedded into PLA to make self-biodegradable plastic

Upgrading Waste Polylactide via Catalyst‐Controlled Tandem Hydrolysis‐Oxidation

Ultrafast Bulk Degradation of Polylactic Acid by Artificially Cultured Diatom Frustules

Depolymerization and Re/Upcycling of Biodegradable PLA Plastics

Cheap Organocatalyst Diphenyl Phosphate for Efficient Chemical Recycling of Poly(Lactic Acid), Other Polyesters and Polycarbonates

Biodegradation and Non-Enzymatic Hydrolysis of Poly(Lactic-co-Glycolic Acid) (PLGA12/88 and PLGA6/94)

Tuning Biodegradation of Poly (lactic acid) (PLA) at Mild Temperature by Blending with Poly (butylene succinate-co-adipate) (PBSA) or Polycaprolactone (PCL)

Polymers produced with depolymerase

Synthesis, Modification and Application of Polylactic Acid

Modulating poly(lactic acid) degradation rate for environmentally sustainable applications

Enzymatic degradation of polylactic acid (PLA)

3D-Printed Enzyme-Embedded Plastics

Novel methods to monitor the biodegradation of polylactic acid (PLA) by Amycolatopsis orientalis and Amycolatopsis thailandensis

Superior sequence-controlled poly(L-lactide)-based bioplastic with tunable seawater biodegradation

Degradable living plastics programmed by engineered spores

Study on Biodegradation Technology for the Structural Change Reaction of Polymer Polylactic Acid

Polylactic Acid/Polycaprolactone Blends: On the Path to Circular Economy, Substituting Single-Use Commodity Plastic Products