Mechanically Robust Polyimide Binder Realizes Stable and High Electrochemical Performance for Micro‐Silicon Anodes in Lithium‐Ion Batteries

Xiaoxiao Liang,Binjie Zhang,NIAZ AHMAD,Xianzhe Yu,Chaoyuan Zeng,Qinxi Dong,Wen Yang

DOI: https://doi.org/10.1002/cssc.202401768

IF: 8.4

2024-10-12

ChemSusChem

Abstract:Silicon is regarded as a highly promising anode material for lithium‐ion batteries, attributed to its substantial theoretical specific capacity. The practical implementation of Si‐anodes is hindered by side reactions and significant volumetric changes, ~300% to 400%, occurring during the lithiation/delithiation processes. Pertinent binders can effectively mitigate the stress resulting from the volumetric exchange in Si‐anodes. Herein, we developed a mechanically stable polyimide binder PI‐CF3 and introduced trifluoromethyl and hydroxyl groups for commercial microparticular Si‐anodes. With the highest Young's modulus of ~921.1 MPa, the binder presented the maximum resilience during the charging and discharging of Micro‐Si, integrating the morphology, and reducing the degree to which the electrode disrupted ion and electric pathways. Moreover, ‐OH and ‐CF3 groups of the binder could potentially interact with the oxide layer at the surface of silicon through H‐bonds resulting in a cross‐linking network to improve interface stability. The as‐prepared PI‐CF3 binder with excellent intrinsic mechanical and electro‐rich groups stabilizes the electrode structure and facilitates fast Li+ transportation. Consequently, at 0.6 Ag−1, the micro‐Si anode produced an initial specific capacity of 1838 mAh g−1 at Si 0.66 mg cm‐2. Besides, at Si 0.78 mg cm‐2 specific capacity retained around 1219 mAh g‐1 over 330 cycles.

chemistry, multidisciplinary,green & sustainable science & technology