Abstract:Fabricate surface-enhanced Raman scattering (SERS) substrate with low cost and high performance through simple method is a challenge and worthy of work. Herein, an excellent Cu2O SERS substrate with porous octahedron structure was synthesized by brief calcining Cu-MOFs in Ar, air and H2/Ar gas environment at 350 °C successively. The as-obtained octahedral Cu2O was utilized as SERS substrate to measure dye molecules and organic pollutants, which exhibited splendid sensitivity for the detection of methylene blue and 4-mercaptopyridine (4-MPY) with the ultralow limit of 5 × 10–9 M and 5 × 10–10 M, respectively. The maximum relative standard deviation for detection of 4-MPY is as low as 12.3%, which is less than limiting step in quantitative SERS (15.0%). The above excellent results are due to outstanding synergistic effect of electromagnetic enhancement of oxygen vacancy on the Cu2O surface and chemical enhancement of the Cu–S bonds formation. The fabricated Cu2O possesses superior sensitivity, selectivity and reproducibility for SERS detection of probe molecules with sulfhydryl groups and may be a prospect candidate in the practical application.Graphical AbstractAn excellent Cu2O SERS substrate with porous octahedron structure was synthesized by simple calcining Cu-MOFs in Ar, air and H2/Ar gas environment at 350 °C successively. The as-prepared Cu2O play significant roles in the enhancement of SERS signals for rich-thiol detection due to outstanding synergistic effect of electromagnetic enhancement of oxygen vacancy on the Cu2O surface and chemical enhancement of the Cu-S bonds formation. The detection limit of 4-Mercaptopyridine (4-MPY) can be as low as 5×10–10 M. The porous octahedral Cu2O will have potential applications in SERS detection as the substrate.

Synthesizing robust cuprous oxide film with adjustable morphologies as surface-enhanced Raman scattering substrate by copper anodization

Rational Electrochemical Design of Cuprous Oxide Hierarchical Microarchitectures and Their Derivatives for SERS Sensing Applications.

Hierarchical nanostructures of cupric oxide on a copper substrate: controllable morphology and wettability

Electromagnetic and Chemical Enhancements of Surface‐Enhanced Raman Scattering Spectra from Cu2O Hexagonal Nanoplates

Roughness induced wettability amplification of novel copper molybdate-branched CuO nanorod arrays by non-aqueous solution method

Preparation and Photoelectric Property of Cuprous Oxide Thin Film with Different Morphologies

Hierarchically rough CuO/Ag composite film with controlled morphology as recyclable SERS-active substrate

Electrochemically generated CuI and CuSCN nanocrystals on Cu surfaces as Raman enhancing substrates

Ion irradiation enhanced Raman scattering on nanoporous copper.

Nanoporous Copper with Tunable Nanoporosity for SERS Applications

Fabrication and characterization of Ag-Cu dendritic periodic array substrate for surface-enhanced Raman scattering

Templated nanoporous copper and nickel: Novel substrates for surface-enhanced Raman scattering

Fabrication of large scale uniform copper-island thin film for ultrasensitive surface enhanced Raman scattering

Magnetically Controllable Flowerlike, Polyhedral Ag-Cu-Co3O4 for Surface-Enhanced Raman Scattering

Surface morphology evolution behavior and SERS performance of Mo-Ag-Cu-Co films

Surface-Enhanced Raman-Scattering (sers) and Surface-Enhanced Resonance Raman-Scattering (serrs) on Hno3-Roughened Copper Foil

Synthesis and superior SERS performance of porous octahedron Cu2O with oxygen vacancy derived from MOFs

Two-step Fabrication of Nanoporous Copper Films with Tunable Morphology for SERS Application

Magnetically Controllable Flowerlike, Polyhedral Ag–Cu–Co 3 O 4 for Surface-Enhanced Raman Scattering

Impact of Surface Hydroxyl Groups on CuO Film Growth by Atomic Layer Deposition

Aligned Copper Nanorod Arrays for Surface-Enhanced Raman Scattering