Abstract:Metal nanodendrites composed of highly branched arms have received great attention as electrocatalysts owing to their reasonably large surface area and the potential existence of low-coordinated sites in high densities. Although significant progress has been made in the synthesis of bimetallic nanodendrites, few works involve a systemconsisting of Pd and Cu, particularly in the case of alloyed nanodendrites. Here, we report a facile and powerful approach for the synthesis of PdCu alloy nanodendrites with tunable composition through varying the molar ratio of the Pd and Cu salt precursors. The key to achieving PdCu alloy nanodendrites is the use of W(CO)(6), which serves as a strong reducing agent. In addition, variation in the molar ratio of the precursors, from Pd rich to Cu rich, leads to shape evolution of the PdCu alloy, moving from a polyhedral to a dendritic nanostructure. This result indicates that galvanic replacement between a Cu rich alloy and a Pd precursor also plays an important role in the formation of PdCu alloy nanodendrites. When used as electrocatalysts for the methanol oxidation reaction (MOR), PdCu alloy nanodendrites exhibit remarkably enhanced catalytic properties relative to commercial Pd/C. Specifically, Pd35Cu65 alloy nanodendrites show the highest specific activity and mass activity for the MOR, 9.3 and 7.6 times higher than that of commercial Pd/C, respectively. This enhancement can be attributed to their dendritic structure and a possible bifunctional mechanism between Pd and Cu.

Synthesis and application of Cu(OH)2 nanowires on nanoporous copper prepared by dealloying Ti50Cu50 and Ti25Zr25Cu50 amorphous alloys

Highly Catalytical Performance of Nanoporous Copper for Electro-Oxidation of Methanol in Alkaline Media

Preparation of Nanoporous Pd/Cuo by Dealloying and Their Electrocatalysis for Methanol in Alkaline Condition

Synthesis of nanoporous CuO/TiO2/Pd-NiO composite catalysts by chemical dealloying and their performance for methanol and ethanol electro-oxidation

Copper Vanadate Nanowires on G-C3n4 Toward Highly Selective Oxidation of Methanol to Dimethoxymethane

PdCu Alloy Nanodendrites with Tunable Composition As Highly Active Electrocatalysts for Methanol Oxidation

Evolution of Palladium/copper Oxide–titanium Dioxide Nanostructures by Dealloying and Their Catalytic Performance for Methanol Electro-Oxidation

Nanoporous copper fabricated from Zr65Cu17.5Fe10Al7.5 amorphous alloy and its electrocatalytic oxidation performance

Nanoporous Nickel-Copper-phosphorus Amorphous Alloy Film for Methanol Electro-Oxidation in Alkaline Medium

Excellent electrocatalytic performance toward methanol oxidation of hierarchical porous NiCu obtained by electrochemical dealloying

Free-Standing Porous Cu-Based Nanowires As Robust Electrocatalyst for Alkaline Oxygen Evolution Reaction

Nanoporous CuO Ribbons Modified by Au Nanoparticles Through Chemical Dealloying and Calcination for CO Oxidation

Fabrication of Nanoporous Copper by Dealloying Amorphous Binary Ti–Cu Alloys in Hydrofluoric Acid Solutions

Gram-Scale Synthesis of Pt-Cu Nanowires with Enhanced Electrocatalytic Activity towards Methanol Oxidation Reaction

From Bimetallic PdCu Nanowires to Ternary PdCu-SnO2 Nanowires: Interface Control for Efficient Ethanol Electrooxidation

Monodisperse Cu@Ptcu Nanocrystals And Their Conversion Into Hollow-Ptcu Nanostructures For Methanol Oxidation

Synthesis of CuO nanowalnuts and nanoribbons from aqueous solution and their catalytic and electrochemical properties

The Role of ZnO Nanowires to Improve Methanol Selectivity on Cu2O Nanocubes During CO2 Electroreduction

Facile Synthesis of Porous PtM (m=cu, Ni) Nanowires and Their Application As Efficient Electrocatalysts for Methanol Electrooxidation

Fabrication and Degradation Properties of Nanoporous Copper with Tunable Pores by Dealloying Amorphous Ti-Cu Alloys with Minor Co Addition

The role of ZnO nanowires to improve methanol selectivity on Cu 2 O nanocubes during CO 2 electroreduction