De‐Passivation and Surface Crystal Plane Reconstruction via Chemical Polishing for Highly Reversible Zinc Anodes

Jin Cao,Xu Wang,Shangshu Qian,Dongdong Zhang,Ding Luo,Lulu Zhang,Jiaqian Qin,Xinyu Zhang,Xuelin Yang,Jun Lu

DOI: https://doi.org/10.1002/adma.202410947

IF: 29.4

2024-09-28

Advanced Materials

Abstract:The chemically polished Zn metal anode (CP‐Zn), achieved through a facile immersion method, effectively removes passivation layers and selectively exposes (002) crystal planes. This process ensures uniform zinc deposition and improved cell stability, demonstrated by over 4600 hours of stable cycling in symmetric cells and high capacity retention in full cells. Despite the widespread adoption of Zn anodes for aqueous energy storage, the presence of an inherent passivation layer and the polycrystalline interface of commercial Zn foil consistently lead to non‐uniform electrodeposition, undermining stability and practicality. Herein, the study introduces a chemically polished Zn metal anode (CP‐Zn) fabricated via a simple immersion method. This "chemically polishing" process can effectively remove the interfacial passivation layer (de‐passivation), providing ample active sites for plating/stripping and ensuring the uniformly distributed electric field and Zn2+ ion flux. Additionally, selective etching during chemical polishing exposes more (002) crystal planes, promoting homogeneous and smooth zinc deposition while suppressing related side reactions. Demonstrated by CP‐Zn anode, the symmetric cell exhibits stable cycling over 4600 h at 1 mA cm−2 and 240 h at 50% depth of discharge (DOD), with a CP‐Zn||VO2 full cell maintaining ≈75.3% capacity retention over 1000 cycles at 3 A g−1. This chemically polishing strategy presents a promising avenue for advancing the commercialization of aqueous zinc‐ion batteries.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology