Highly active and CO-resistant PdRuMo/C with a wide potential-stable window toward alkaline hydrogen oxidation reaction
Chunxiao Chai,Haoliang Huang,Hao Yang,Jiaqi Qin,Chongyun Sun,Yongpeng Li,Zhaoqi Wang,Xinwei Zhao,Zhongyu Qiu,Tiantian Li,Jiahuan Li,Rui Gao,Yang Zhao,Yuanyuan Cong,Yang Lv,Yujiang Song
DOI: https://doi.org/10.1016/j.cej.2024.158580
IF: 15.1
2024-12-16
Chemical Engineering Journal
Abstract:The substitution of platinum with low-cost ruthenium is of interest toward alkaline hydrogen oxidation reaction (HOR). However, Ru-based HOR electrocatalysts confront the hurdles of ruthenium oxidation, low activity and CO poisoning. Herein, we report the synthesis of 2–3 nm PdRuMo alloy particles evenly distributed on carbon, followed by in situ evolution into PdH x RuMo/C owning to the formation of surface PdH x in the presence of H 2 . Remarkably, PdRuMo/C remains stable up to 0.78 V vs. RHE during HOR process in that Ru accepts electrons from Mo and Pd, and H species spills over to protect Ru from being oxidized. To the best of knowledge, PdRuMo/C possesses the widest potential-stable window among Ru-based HOR electrocatalysts. In addition, PdRuMo/C exhibits an exceptional activity in terms of mass specific exchange current density of 849.6 A g metal -1 toward alkaline HOR, which is 2.6 and 3.0 times of that of commercial Pt/C and Ru/C, respectively. The excellent HOR activity originates from high electrochemically active surface area (164.9 m 2 g metal -1 ), surface low-coordination atoms, and strengthened hydroxide binding energy as well as weakened hydrogen binding energy. Furthermore, PdRuMo/C remains 97.2 % of the initial current density in the presence of 1000 ppm CO superior to that of commercial Pt/C (77.7 %) and Ru/C (88.5 %). The remarkable CO-resistance is correlated with weakened CO adsorption as evidenced by negatively shifted CO-stripping peak and d-band center downshift of 0.35 eV. Density functional theory (DFT) further deepens the understanding on the origins of HOR potential stability, activity, reaction mechanism, and CO-resistance of PdRuMo/C. Finally, the high HOR activity of PdRuMo/C was verified in AEMFCs with a peak power density of 344.4 mW cm −2 .
engineering, chemical, environmental