On the hydrogen embrittlement behavior of nickel-based alloys: Alloys 718 and 725

Xu Lu,Yan Ma,Dong Wang

DOI: https://doi.org/10.1016/j.msea.2020.139785

2020-08-01

Abstract:<p>Nickel-based superalloys have attracted immense attention in the oil and gas industry due to their outstanding combination of mechanical properties and corrosion resistance. In corrosive service environment, hydrogen embrittlement is a severe issue. In the present work, the susceptibility of two precipitation-hardened nickel-based alloys, <em>i.e.</em>, Alloy 718 and Alloy 725, to hydrogen embrittlement was studied using slow strain-rate tensile test and advanced characterization techniques. The mechanical properties and fracture behavior of these two alloys were compared in both hydrogen-free and hydrogen-charged conditions. In the presence of hydrogen, Alloy 718 failed prevalently through a combination of transgranular and intergranular cracking behavior, while Alloy 725 failed primarily through intergranular failure with a considerably lower resistance to hydrogen embrittlement. This distinction was attributed to their different microstructures and different types of precipitates along grain boundaries. Specifically, in Alloy 725, the decoration of (Cr, Mo)-rich precipitates at grain boundaries distort the local structures and cause such boundaries to be vulnerable to hydrogen attack, thus promoting intergranular cracking.</p>

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

This paper attempts to address the issue of hydrogen embrittlement behavior of nickel-based alloys (specifically Alloy 718 and Alloy 725) in corrosive environments. Specifically, the study aims to compare the mechanical properties and fracture behavior of these two alloys under hydrogen-free and hydrogen-charged conditions through slow strain rate tensile tests and advanced microstructural characterization techniques, thereby gaining a deeper understanding of the impact of hydrogen on these precipitation-hardened nickel-based alloys. The study focuses on the following points:

1. **Hydrogen Embrittlement Sensitivity**: Evaluate the hydrogen embrittlement sensitivity of Alloy 718 and Alloy 725 in hydrogen environments.
2. **Changes in Mechanical Properties**: Compare the changes in yield strength, ultimate tensile strength, and total elongation of the two alloys under hydrogen-free and hydrogen-charged conditions.
3. **Fracture Modes**: Analyze the fracture modes of the two alloys under different conditions, including intergranular and transgranular fracture behavior.
4. **Microstructural Influence**: Investigate the influence of different microstructural features (such as grain size, type, and distribution of precipitates) on hydrogen embrittlement behavior, particularly the role of grain boundary precipitates.

Through these studies, the authors hope to provide scientific evidence for the application of nickel-based alloys in the oil and gas industry, especially in highly corrosive and high-pressure high-temperature environments, on how to select and optimize materials to prevent early failure and catastrophic accidents caused by hydrogen embrittlement.