Roles of Fast‐Ion Conductor LiTaO 3 Modifying Ni‐rich Cathode Material for Li‐Ion Batteries

Yuefeng Su,Gang Chen,Lai Chen,Qi Shi,Zhao Lv,Yun Lu,Liying Bao,Ning Li,Shi Chen,Feng Wu

DOI: https://doi.org/10.1002/cssc.202100156

IF: 8.4

2021-03-18

ChemSusChem

Abstract:Limited cycling stability hampers the commercial application of Ni‐rich materials, which are regarded as one of the most promising cathode materials for Li‐ion batteries. We modified Ni‐rich LiNi 0.9 Co 0.06 Mn 0.04 O 2 layered cathode with different amounts of LiTaO 3 and explored the influences of fast‐ion conductor material on cathode materials. Detailed analysis of the materials revealed the formation of a uniformly epitaxial LiTaO 3 coating layer and a little Ta 5+ doping into the lattice structure of Ni‐rich materials. The coating‐layer thickness increases with the amount of LiTaO 3 added, protecting the electrode from erosion by electrolyte and suppressing undesired parasitic reactions on the cathode‐electrolyte interface. Meanwhile, the doped Ta 5+ increases the interplanar spacing of materials, accelerating Li + transfer. Using the positive synergistic effects of LiTaO 3 ‐coating and Ta 5+ ‐doping, improved capacity retentions of the modified materials, especially for 0.25 and 0.5 wt% coated Ni‐rich materials, were obtained after long‐term cycling, showing the potential applications of LiTaO 3 modification. Further, the relations between one excessively thick coating layer and transfer of Li + /electron between the cathode and electrolyte was established, proving that very thick coating layers, even layers containing Li‐ion, have adverse effects on electrochemical performances. This finding may help us to understand the roles of the coating layer better.

chemistry, multidisciplinary,green & sustainable science & technology

What problem does this paper attempt to address?

The problem that this paper attempts to solve is to improve the cycling stability and electrochemical performance of high - nickel (Ni - rich) cathode materials in lithium - ion batteries. Specifically, high - nickel materials (such as LiNi₀.₉Co₀.₀₆Mn₀.₀₄O₂) exhibit poor cycling stability in practical applications due to their high nickel content, which limits their commercial applications. To improve this problem, researchers have attempted to modify high - nickel cathode materials with different amounts of the fast - ion conductor LiTaO₃ and explored the influence of this modified material on the cathode material.

### Summary of main problems:
1. **Poor cycling stability**: High - nickel materials experience severe capacity decay after long - term charge - discharge cycles.
2. **Poor electrochemical performance**: The performance of high - nickel materials under high - rate charge - discharge conditions is not satisfactory.
3. **Interfacial side reactions**: The interfacial side reactions between high - nickel materials and the electrolyte lead to a decline in material performance.

### Solutions:
- **LiTaO₃ coating**: By introducing a LiTaO₃ coating, a uniform protective layer is formed to prevent the electrolyte from eroding the electrode material and suppress unwanted parasitic reactions.
- **Ta⁵⁺ doping**: A small amount of Ta⁵⁺ is doped into the lattice structure of high - nickel materials, increasing the inter - layer spacing, accelerating Li⁺ transport, and improving the structural stability of the material.

### Experimental results:
- The modified materials show better capacity retention in long - cycle tests, especially in samples modified with 0.25 wt% and 0.5 wt% LiTaO₃.
- An overly thick coating will, on the contrary, impede the transport of Li⁺ and electrons and reduce electrochemical performance, so the coating thickness needs to be optimized.

### Conclusion:
Appropriate LiTaO₃ coating and Ta⁵⁺ doping can effectively improve the cycling stability and rate performance of high - nickel cathode materials, providing new ideas for the practical application of high - nickel materials. At the same time, the research also reveals the negative impact of an overly thick coating on electrochemical performance, which helps to better understand the role of coatings in cathode materials.