Superior strength–toughness synergy of heterogeneous TiB2p/AZ91 composites containing hard/soft zones via tailoring bimodal grain structure

Peng Xiao,Qiqiang Zhao,Yupeng Sheng,Cuicui Yang,Yimin Gao,Wenyu Wu,Zhiwei Liu,Yanliang Yi

DOI: https://doi.org/10.1016/j.msea.2023.145775

2023-11-01

Abstract:Magnesium matrix composites show great prospects due to lightweight and high specific strength, but strength-toughness tradeoff has limited their engineering applications. Here, a novel strategy for strengthening and toughening TiB2p/AZ91 (TiB2p: TiB2 particles) Mg matrix composites via tailoring heterogeneous configuration containing hard/soft zones and bimodal grain structure is proposed. The results show that hot extrusion deformation can achieve heterogeneous structure of hard and soft zones resulting from alternating arrangement TiB2p, which induces the formation of coarse and fine grain zones. With the decrease of extrusion temperature, both the hard zone spacing and the number of coarse grains have a great decrease. In particular, TiB2p/AZ91 composites extruded at 400 °C and 350 °C exhibit obvious bimodal grain structure, while almost uniform fine grains are obtained in the composites extruded at 300 °C. This contributes to the excellent comprehensive mechanical properties of TiB2p/AZ91 composites at 400 °C and 350 °C, with UTS of 345 MPa, 388 MPa, and elongation of 12.1%, 10.1%, respectively. Compared with AZ91 alloy, the strength of composites extruded at 400 °C and 350 °C is significantly improved, while the ductility is not sacrificed, indicating that superior strength–toughness synergy is achieved. The improved toughness is ascribed to the increased strain hardening capacity, suppressing and deflecting effects of the hard zones on the crack propagation. Lower extrusion (300 °C), however, leads to the reduced toughness of the composites, which is due to the premature initiation of cracks caused by smaller hard zone spacing and large amount of precipitated phase.

materials science, multidisciplinary,nanoscience & nanotechnology,metallurgy & metallurgical engineering

What problem does this paper attempt to address?

The paper primarily aims to address the application bottleneck of magnesium matrix composites (Mg matrix composites) in the field of high-end equipment manufacturing. Specifically, although ceramic particle-reinforced magnesium alloys have advantages such as lightweight and high specific strength, these ceramic particles (e.g., TiB2 particles) improve the strength of magnesium alloys while reducing their plasticity and toughness, thereby affecting their processing performance and service reliability. Therefore, developing magnesium matrix composites with both high strength and high toughness is of great significance for achieving lightweight in high-end manufacturing and has become an urgent problem to solve.

The paper proposes a novel method to improve the comprehensive mechanical properties of TiB2p/AZ91 magnesium matrix composites by adjusting the heterogeneous structure (including hard and soft regions as well as bimodal grain structures) formed during the hot extrusion process. The study found that the composites extruded at 400°C and 350°C exhibited excellent strength-toughness synergy, with tensile strengths reaching 345 MPa and 388 MPa, and elongations of 12.1% and 10.1%, respectively, without sacrificing their ductility. In contrast, the composites extruded at 300°C, although having higher strength, showed a significant decrease in toughness.

In summary, the paper aims to overcome the contradiction between strength and plasticity/toughness in traditional magnesium matrix composites by regulating the distribution of hard and soft regions and grain size within the microstructure of the composites, thereby achieving a comprehensive improvement in material performance.