A Carbonyl Iron/Carbon Fiber Material for Electromagnetic Wave Absorption

Meng-Jey Youh,Hung-Chih Wu,Wang-Hua Lin,Sheng-Cheng Chiu,Chien-Fa Huang,Hsin-Chih Yu,Jen-Sung Hsu,Yuan-Yao Li

DOI: https://doi.org/10.1166/jnn.2011.3584

2011-03-01

Journal of Nanoscience and Nanotechnology

Abstract:A carbonyl iron/carbon fiber material consisting of carbon fibers grown on micrometer-sized carbonyl iron sphere, was synthesized by chemical vapor deposition using a mixture of C2H2 and H2. The hollow-core carbon fibers (outer diameter: 140 nm and inner diameter: 40 nm) were composed of well-ordered graphene layers which were almost parallel to the long axis of the fibers. A composite (2 mm thick) consisting of the carbonyl iron/carbon fibers and epoxy resin demonstrated excellent electromagnetic (EM) wave absorption. Minimum reflection losses of -36 dB (99.95% of EM wave absorption) at 7.6 GHz and -32 dB (99.92% of EM wave absorption) at 34.1 GHz were achieved. The well-dispersed and network-like carbon fibers in the resin matrix affected the dielectric loss of the EM wave while the carbonyl iron affected the magnetic loss.