Fabrication of Graphene Oxide/Fiber Reinforced Polymer Cement Mortar with Remarkable Repair and Bonding Properties
Yibo Gao,Jianlin Luo,Shike Yuan,Jigang Zhang,Song Gao,Min Zhu,Zhiqing Li,Xiaoyang Zhou
DOI: https://doi.org/10.1016/j.jmrt.2023.05.144
IF: 6.267
2023-05-20
Journal of Materials Research and Technology
Abstract:It is cost-effective and low-carbon emission using high performance mortar to repair and protect damaged structures. Here, graphene oxide (GO)/steel fiber (SF) reinforced ethylene vinyl acetate (EVA) polymer compound sulfoaluminate cement repair mortar (GOCRM) was directly prepared by water-reducer sonication dispersion and subsequent shear mix method. The workability, mechanical properties, and durability of GOCRM were systematically investigated along with microstructure and micro/nano enhancement mechanism evaluation. The flowability, initial/final setting time, 1 day/28 days flexural, 1 day/28 days compressive, interfacial bonding strength ( f b ), 90 days drying shrinkage, 3 days water absorption rate, contact angle and migration coefficient of chloride ion of GOCRM at 0.03% GO dosage reach 192.0 mm, 35 min/53 min, 8 MPa/19.9 MPa, 21.3 MPa/79.3 MPa, 4.93 MPa, 1.051×10 -4 , 0.1%, 80.96° and 2.322×10 -13 m 2 /s, respectively. Microscopic morphology, Fourier transform infrared spectroscopy, and X-ray diffraction spectra of mortars with varied curing ages demonstrate that sulfoaluminate cement, EVA, GO incorporation can improve the microstructure in interiors and at interfaces of mortars by filling micro-pores between products and promoting hydration degree. Accordingly, tighter bonding surface, higher f b and superior bond durability between GOCRM and the old substrate are achieved. These indicate that GOCRM can advantageously serve as high-performance repair mortar with superior fast repair capability, and long-term repair stability.
materials science, multidisciplinary,metallurgy & metallurgical engineering