Selective recovery of strontium from oilfield water by ion-imprinted alginate microspheres modified with thioglycollic acid

Can Liu,Xiaoping Yu,Chi Ma,Yafei Guo,Tianlong Deng

DOI: https://doi.org/10.1016/j.cej.2020.128267

IF: 15.1

2021-04-01

Chemical Engineering Journal

Abstract:<p>The efficient recovery of Sr²⁺ from brine is a great challenge due to the interference of a large number of coexisting ions. Herein, a new-type spherical Sr²⁺ adsorbent with a diameter of about 2-3 mm was developed by the ion-imprinting method using low-cost and high hydrophilic sodium alginate (SA). It was found that although SA could be granulated in HCl solution, it showed no adsorption ability for Sr²⁺. However, when SA was ion-imprinted with Sr²⁺ and then eluted with HCl, the material exhibited excellent adsorption performance. Especially, after modification with thioglycollic acid, the maximum adsorption capacity reached approximately 177 mg·g^-1, which was far higher than that of the spherical materials reported at present. The Sr²⁺ in the material could be eluted easily with 0.05 mol·L^-1 HCl at an eluent dosage of only 0.02 L·g^-1, and the Sr²⁺ concentration in the eluate was nearly 25 times higher than that in the original solution. Because of the ion-sieve effect, the developed adsorbent presented high stability and selectivity when used for Sr²⁺ recovery from oilfield water. The attenuation of adsorption capacity was only 0.42% after five adsorption-desorption. The separation factors between Sr²⁺ and other ions were all higher than 54, indicating that the selective recovery of Sr²⁺ is almost unaffected by coexisting Na⁺, K⁺, Mg²⁺, and Ca²⁺. All these properties suggest that the proposed material has excellent properties and can be used as a candidate for selective recovery of Sr²⁺ from oilfield water or other liquid strontium resources.</p>

engineering, chemical, environmental