Abstract:The BiVO4/HNTs hybrid photocatalysts were synthesized by liquid phase precipitation using natural halloysite nanotubes (HNTs) as supporter and Bi(NO3)·5H2O as resource of Bi. XRD, scanning electron microscopy (SEM), transmission electron microscopy, HRTEM, x-ray photo electron spectroscopy and UV-Vis DRS were used to characterize the samples prepared at different calcination temperatures, and the effects of crystallization, Brunauer-Emmett-Teller specific surface area and morphological structure on the photoactivity were investigated. Results reveal that increasing calcination temperature can accelerate the transition of BiVO4 from tetragonal to monoclinic and also decrease the surface area of BiVO4/HNTs. The SEM results showed that BiVO4 was successfully coated on HNTs surface with ellipsoid or near rod like morphology, and the obtained BiVO4/HNTs had regular nanotube morphology. HRTEM results showed that, the regular fringe spacing of the lattice planes are about 0.474 and 0.364 nm, which is consistent with the (110) and (200) plane of the monoclinic and tetragonal BiVO4, confirming the exiting of mixed crystal structure in BiVO4/HNTs. BiVO4 with tetragonal phase (80.02%) and monoclinic phase (19.98%) mixed crystal is loaded on the surface of HNTs with calcinations at 400 °C for 2 h. The structure and Si (Al)-O bond of HNTs can be obviously changed over the calcination temperature of 400 °C. The effect of calcination temperature on photocatalytic reactivity of samples was investigated by degradation of dyes (MB, MO and RhB) under simulated solar light. And the sample calcined at 400 °C with the better mixed crystalline structure and larger specific surface area exhibits significant activity with the removal rate of MB and RhB up to 100% within 4 h. The degradation of MB follows the first order kinetic model. BiVO4/HNTs photocatalysts with the band gap of 2.34 eV has higher photocatalytic reaction rate and better sedimentation performance than Degussa P25. The photocatalytic degradation efficiency of BiVO4/HNTs for MB was no significant reduction after four times recycles.

Synthesis of (NH4)2Ta2O3F6 mesocrystals via a hydrothermal route and their conversion to TaO2F and Ta2O5 mesocrystals for photocatalytic dyes degradation

Mesoporous MgTa 2o 6 thin films with enhanced photocatalytic activity: On the interplay between crystallinity and mesostructure

Ordered Mesoporous Thin Films Of Rutile Tio2 Nanocrystals Mixed With Amorphous Ta2o5

Enhanced photocatalytic activity of nonstoichiometric crystalline TaO2F and Ta2O5 with carbon coating

Well-dispersed mesoporous Ta2O5 submicrospheres: Enhanced photocatalytic activity by tuning heating rate at calcination

Preparation, characterization and photocatalytic activity of N-doped NaTaO3 nanocubes

Self-assembly and Photocatalysis of Mesoporous TiO 2 Nanocrystal Clusters

Hydrothermal Preparation of Nb-doped NaTaO3 with Enhanced Photocatalytic Activity for Removal of Organic Dye

Monomolecular-Layer Ba5Ta4O15 Nanosheets: Synthesis and Investigation of Photocatalytic Properties

Construction of amorphous In2S3 decorated Ta2O5-x mesocrystals for enhanced photocatalytic tetracycline degradation

(001)-Exposed TiO2 Microcrystals Decorated with Few-Layer Nanobelts for Enhanced Photocatalytic Activity

TiO2 Intercalated Talc Nanocomposite: Preparation, Characterization, and Its Photocatalytic Performance

Effect of Solvents and Reaction Parameters on the Morphology of Ta2O5 and Photocatalytic Activity

Room‐Temperature Hydrolysis of Potassium Titanyl Oxalate and Water‐Assisted Crystallization for TiO2 with High Photocatalytic Activity

Facile Synthesis of Ni-doped TiO2ultrathin Nanobelt Arrays with Enhanced Photocatalytic Performance

Topotactic formation of poriferous (Al,C)–Ta2O5 mesocrystals for improved visible-light photocatalysis

Construction of metallic nanocrystalline TaB2 coupled with TiO2 for enhanced photocatalytic degradation

General synthesis of single‐crystalline Ta2O5 nanorods towards enhanced photocatalytic H2 production activity

Crystallinity and Photocatalytic Properties of BiVO4/halloysite Nanotubes Hybrid Catalysts for Sunlight-Driven Decomposition of Dyes from Aqueous Solution

Synthesis and photocatalytic activity of N-doped NaTaO3 compounds calcined at low temperature

One-step synthesis of oxygen-defects modified Ta2O5 nanosheets with high photocatalytic performance by chemical vapor deposition method