Dual‐Doping and Synergism toward High‐Performance Seawater Electrolysis

Jinfa Chang,Guanzhi Wang,Zhenzhong Yang,Boyang Li,Qi Wang,Ruslan Kuliiev,Nina Orlovskaya,Meng Gu,Yingge Du,Guofeng Wang,Yang Yang

DOI: https://doi.org/10.1002/adma.202101425

IF: 29.4

2021-07-08

Advanced Materials

Abstract:<p>Hydrogen (H₂) production from direct seawater electrolysis is an economically appealing yet fundamentally and technically challenging approach to harvest clean energy. The current seawater electrolysis technology is significantly hindered by the poor stability and low selectivity of the oxygen evolution reaction (OER) due to the competition with chlorine evolution reaction in practical application. Herein, iron and phosphor dual-doped nickel selenide nanoporous films (Fe,P-NiSe₂ NFs) are rationally designed as bifunctional catalysts for high-efficiency direct seawater electrolysis. The doping of Fe cation increases the selectivity and Faraday efficiency (FE) of the OER. While the doping of P anions improves the electronic conductivity and prevents the dissolution of selenide by forming a passivation layer containing P–O species. The Fe-dopant is identified as the primary active site for the hydrogen evolution reaction, and meanwhile, stimulates the adjacent Ni atoms as active centers for the OER. The experimental analyses and theoretical calculations provide an insightful understanding of the roles of dual-dopants in boosting seawater electrolysis. As a result, a current density of 0.8 A cm⁻² is archived at 1.8 V with high OER selectivity and long-term stability for over 200 h, which surpasses the benchmarking platinum-group-metals-free electrolyzers.</p>

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology

What problem does this paper attempt to address?

The paper aims to address several key issues in the process of direct seawater electrolysis. Specifically:

1. **Competition between Oxygen Evolution Reaction (OER) and Chlorine Evolution Reaction (CER)**: In the process of seawater electrolysis, there is competition between the oxygen evolution reaction and the chlorine evolution reaction at the anode because their thermodynamic potentials are very close. This competition can reduce the Faradaic efficiency of the oxygen evolution reaction and increase the cell voltage.

2. **Poor stability of electrode materials**: The existing electrode materials lack sufficient stability during long-term operation, which hinders the continuous production of hydrogen.

3. **Biofouling and trace metal deposition**: These issues can also affect the performance of seawater electrolysis, especially during long-term operation.

To address the above issues, the research team designed an iron and phosphorus co-doped nickel selenide nanoporous thin film (Fe,P-NiSe₂ NFs) as a bifunctional catalyst for efficient direct seawater electrolysis. This co-doped material can improve the selectivity and Faradaic efficiency of the oxygen evolution reaction and enhance electronic conductivity and prevent selenide dissolution by forming a passivation layer containing P-O species. Experimental results show that this catalyst achieved a current density of 0.8 A/cm² at a voltage of 1.8 volts and exhibited high selectivity and stability for over 200 hours, surpassing the standard performance of current non-platinum group metal electrolyzers.