Dual Ionic Liquid-Functionalized Cellulosic Materials: Thermal, Conductive, and Morphological Properties

Elizabeth A. Hays,Gabrielle Eicher,Abneris Morales,David Salas-de la Cruz,Kevin M. Miller

DOI: https://doi.org/10.1021/acsapm.3c02815

2024-02-16

ACS Applied Polymer Materials

Abstract:Dual ionic liquid-substituted cellulosic materials were prepared by coupling a series of alkyne-terminated imidazoles with variable carbon spacer with azide-functionalized cellulose, followed by quaternization and anion exchange. All three of the [NTf2]-bearing cellulosic materials exhibited T g values below zero and could be cast as flexible films, which exhibited stress at break values exceeding 2.3 MPa with strain at break values up to 252%. X-ray scattering analyses indicated the amorphous nature of the cellulosic materials with three scattering peaks observed, from high-to-low q, corresponding to the amorphous halo, anion-to-anion distance, and the distance between ion aggregates, respectively. The highest degree of ionic aggregation was found to exist in the CELL-C12-NTf 2 material, presumably due to the longer alkyl tethers causing more uniformity in the interaggregate spacing. The conductivity of the films was found to be on the order of 10–5–10–6 S/cm at 30 °C. A slower increase in conductivity with temperature was observed for systems where ionic aggregation was the strongest.

polymer science,materials science, multidisciplinary