Preparation of CsPbBr(3 )perovskite nanocrystals with controllable morphology and in-situ photoluminescenceof formation kinetics
Chen Xue-Lian,Ju Bo,Jiao Hu-Po,Li Yan,Zhong Yu-Jie
DOI: https://doi.org/10.7498/aps.71.20212228
IF: 0.906
2022-01-01
Acta Physica Sinica
Abstract:Cesium-lead halide perovskite nanocrystals (CsPbX3 (X = Br, Cl, I) PNCs) have become ideal luminescentmaterials for wide color gamut display devices, white LED lighting and high-efficiency solar cells, due toadjustable energy band gap, high fluorescence quantum yield, narrow fluorescence emission peak, and ultra-highdefect tolerance. The preparation of CsPbX3 PNCs with controllable size and morphology is a prerequisite forobtaining efficient and stable photovoltaic/photovoltaic devices. In this report, the CsPbBr3 PNCs withdifferent shapes are prepared by adding different concentrations of dodecanedioic acid (DDDA) ligands at roomtemperature through using ligand-assisted reprecipitation method. Utilizing the X-ray diffractometer,transmission electron microscopy, ultraviolet spectrophotometer, fluorescence spectrometers (PL), the phasestructure, microstructure and optical properties of the nanocrystals are investigated. The results show that thepresence of DDDA ligands have no influence on the phase structure of nanocrystal products, they all present acubic phase structure. Surprisingly, the morphology of the nanocrystals gradually transforms from nanocubesinto nanoplatelets with ???5 layers in thickness as the concentration of DDDA increases. In addition, the PLspectrum shows a significant blue shift from 509 nm to 478 nm. By using the in-situ homemade PL device withultra-high time resolution (???100 ms), the real-time monitoring PL spectra of nanocrystals in the formationprocess are measured. The results demonstrate that nanocrystals undergo rapid nucleation and focusing of sizedistribution growth to generate nanocubes in the absence of DDDA ligand. When the DDDA ligand is present,nanocrystals are mainly nanoplatelets in the early growth stage due to the decelerated reaction. As the reactionproceeds, nanocubes can emerge and grow gradually while the nanoplatelets disappear when the concentrationsof DDDA ligands are 25% and 50%. As the concentration is further increased to 75%, almost nanoplateletscould be formed after the nucleation stage and growth stage. Unexpectedly, preformed nanoplatelets areunstable for the prolonged reaction time as a result of the high surface energy, and they will eventuallytransform into isotropic nanocubes through dissolution-recrystallization pathway, indicating that the process inthe later stage is controlled mainly by thermodynamics. Our findings offer an efficient strategy to synthesize theperovskite nanocrystals with controllable size and morphology.