Effect of Fiber Loading on Mechanical and Flame-Retardant Properties of Poplar-Fiber-Reinforced Gypsum Composites

Yunpeng Ye,Qinqin Huang,Xingong Li

DOI: https://doi.org/10.3390/molecules29112674

IF: 4.6

2024-06-06

Molecules

Abstract:Gypsum-based composites were prepared via a slurry casting process using construction gypsum as the binding material and poplar fibers as reinforcing material. The effects of different fiber content and curing time on the mechanical properties, water resistance, and flame retardancy of these composites were investigated, and the influence mechanism was characterized by infrared spectroscopy, scanning electron microscopy, and X-ray diffractometry. The results showed that the best composite mechanical strength was achieved with 10% poplar fiber- content, and the absolute dry flexural and compressive strengths reached 3.59 and 8.06 MPa, respectively. Compared with pure gypsum, the flexural strength and compressive strength increased by 10% and 19%, respectively. The inclusion of fibers somewhat prevented the migration of free water within the composites and enhanced their water resistance. At 10% fiber content, the composite's 24 h water absorption rate was 34.3%, 8% lower than that of pure gypsum, with a softening coefficient of 0.55. However, fiber content increases the porosity of gypsum-based composites. When heated, this increased porosity accelerates' heat conduction within the matrix, raising the peak and total exothermic rates, thereby weakening the composites' inherently flame-retardant properties. Poplar-fiber-reinforced gypsum-based composites offered superior performance in commercial applications, compared to pure gypsum board, providing a sustainable and green alternative for ceilings, partitions, and other applications, while broadening the prospects for gypsum-based composites in the engineering field.

chemistry, multidisciplinary,biochemistry & molecular biology

What problem does this paper attempt to address?

The paper mainly explores the effects of different contents of poplar wood fibers on the mechanical properties, flame retardancy, and waterproof performance of gypsum-based composites.

### Research Background and Objectives

With the development of green building systems, the demand for using environmentally friendly materials to enhance building materials is increasing. Although gypsum products have excellent properties such as fire resistance and light weight, their low strength and poor waterproof performance limit their application in the construction field. To overcome these shortcomings, researchers typically add various synthetic or natural fibers to improve the physical and mechanical properties of the composites.

### Research Content

In this study, high-content poplar wood fiber-reinforced gypsum-based composites were prepared by adjusting the water-to-gypsum ratio and wood-to-gypsum ratio, using construction gypsum as the matrix material and poplar wood fibers as the filler material. The effects of different poplar wood fiber contents (from 0% to 15%) and curing times (7 days, 14 days, 28 days) on the mechanical properties (flexural strength, compressive strength) and waterproof performance (water absorption rate, softening coefficient) of the composites were investigated. The mechanisms were explored through infrared spectroscopy, scanning electron microscopy, and X-ray diffraction analysis.

### Main Findings

- **Mechanical Properties**: When the poplar wood fiber content was 10%, the composites achieved the best mechanical properties, with flexural strength and compressive strength reaching 3.59 MPa and 8.06 MPa, respectively, which were 10% and 19% higher than those of pure gypsum.
- **Waterproof Performance**: The addition of poplar wood fibers enhanced the waterproof performance of the composites to a certain extent. The 24-hour water absorption rate of the composite with 10% fiber content was 34.3%, which was 8% lower than that of pure gypsum, and the softening coefficient was 0.55.
- **Flame Retardancy**: The increase in poplar wood fiber content led to an increase in the porosity of the gypsum-based composites, which accelerated the heat conduction within the matrix during heating, thereby weakening the inherent flame retardancy of the composites.
- **XRD Analysis**: X-ray diffraction analysis showed that the poplar wood fiber content within the experimental range had little effect on the internal crystals of the composites.

In summary, this study aims to improve the mechanical properties and waterproof performance of gypsum-based composites by adding different contents of poplar wood fibers, providing sustainable solutions for green buildings.