Abstract:Fe/N/C catalysts, synthesized through the pyrolysis of Fe-doped metal-organic framework (MOF) precursors, have attracted extensive attention owing to their promising oxygen reduction reaction (ORR) catalytic activity in fuel cells and/or metal-air batteries. However, post-treatments (acid washing, second pyrolysis, and so on) are unavoidable to improve ORR catalytic activity and stability. The method for introducing Fe3+ sources (anhydrous FeCl3) into the MOF structure, in particular, is a critical step that can avoid time-consuming post-treatments and result in more exposed Fe-Nx active sites. Herein, three different Fe doping strategies were systematically investigated to explore their influence on the types of active sites formed and ORR performance. Fe-NC(Zn2+), synthesized by one-step pyrolysis of Fe doped ZIF-8 (Zn2+) precursor which was obtained by adding the anhydrous FeCl3 source into the Zn(NO3)2•6H2O/methanol solution before mixing, possessed the highest Fe-Nx active sites due to the high-efficiency substitution of Zn2+ ions with Fe3+ ions during ZIF-8 growth, the strong interaction between Fe3+ ions and N atoms of 2-Methylimidazole (2-MIm), and ZIF-8's micropore confinement effect. As a result, Fe-NC(Zn2+) presented high ORR activity in the entire pH range (pH = 1, 7, and 13). At pH = 13, Fe-NC(Zn2+) exhibited a half-wave potential (E1/2) of 0.95 V (vs. reversible hydrogen electrode), which was 70 mV higher than that of commercial Pt/C. More importantly, Fe-NC(Zn2+) showed superior ORR stability in neutral media without performance loss after 5,000 cycles. A record-high open-circuit voltage (1.9 V) was obtained when Fe-NC(Zn2+) was used as a cathodic catalyst in assembled Mg-air batteries in neutral media. The assembled liquid and all-solid Mg-air batteries with high performance indicated that Fe-NC(Zn2+) has enormous potential for use in flexible and wearable Mg-air batteries.

Fe, N, S co-doped carbon network derived from acetate-modified Fe-ZIF-8 for oxygen reduction reaction

ZIF-8 with Ferrocene Encapsulated: A Promising Precursor to Single-Atom Fe Embedded Nitrogen-Doped Carbon As Highly Efficient Catalyst for Oxygen Electroreduction

Fe3C cluster-promoted single-atom Fe, N doped carbon for oxygen-reduction reaction

Highly Active Cofe Alloy Nanoparticlesencapsulated in N-Doped Carbon Nanostructures for Oxygen Reduction Reaction in Both Alkaline and Acidic Media

Synergistic Cooperation between Atomically Dispersed Zn and Fe on Porous Nitrogen-doped Carbon for Boosting Oxygen Reduction Reaction

Fe/N-Doped Carbon Framework Derived from ZIF-8 on Graphene Oxide for Efficient Oxygen Reduction Reaction

Coexisting Fe single atoms and nanoparticles on hierarchically porous carbon for high-efficiency oxygen reduction reaction and Zn-air batteries

Fe Single Atoms Anchored on N-doped Mesoporous Carbon Microspheres for Promoted Oxygen Reduction Reaction

Nitrogen-carbon-encapsulated Fe3C nanoparticles as highly efficient earth-abundant oxygen reduction electrocatalysts

Nitrogen-carbon-encapsulated Fe 3 C Nanoparticles As Highly Efficient Earth-Abundant Oxygen Reduction Electrocatalysts

Sulfate Ions Induced Concave Porous S‐N Co‐Doped Carbon Confined FeC x Nanoclusters with Fe‐N 4 Sites for Efficient Oxygen Reduction in Alkaline and Acid Media

ZIF-8-derived Fe/P/N-co-doped Carbon as Efficient Electrocatalysts for Oxygen Reduction Reaction and Zinc-air Batteries

A Versatile Approach to Boost Oxygen Reduction of Fe‐N 4 Sites by Controllably Incorporating Sulfur Functionality

Influence of different Fe doping strategies on modulating active sites and oxygen reduction reaction performance of Fe, N-doped carbonaceous catalysts

Covalent organic framework‐derived Fe, Co‐nitrogen codoped carbon as a bifunctional electrocatalyst for rechargeable efficient Zn–air batteries

Rational design of Fe, N co-doped porous carbon derived from conjugated microporous polymer as an electrocatalytic platform for oxygen reduction reaction

Boosting Oxygen Reduction Catalysis with Hierarchically Porous Fe-Doped Carbon by Chemical Vapor Deposition in Zn–Air Batteries

Hierarchically porous Fe/N/S/C nanospheres with high-content of Fe-Nx for enhanced ORR and Zn-air battery performance

Design of nanosheet/nanotube composites of Fe, N-doped carbon for enhanced oxygen reduction in zinc-air batteries

Electrospun Carbon Nanofibers Loaded with Atomic FeN x /Fe 2 O 3 Active Sites for Efficient Oxygen Reduction Reaction in Both Acidic and Alkaline Media

Ionic liquid-derived Fe, N, S, F multiple heteroatom-doped carbon materials for enhanced oxygen reduction reaction