Highly Thermally Conductive and Superior Electrical Insulation Polymer Composites via In Situ Thermal Expansion of Expanded Graphite and In Situ Oxidation of Aluminum Nanoflakes

Shuangqiao Yang,Qi Wang,Bianying Wen

DOI: https://doi.org/10.1021/acsami.0c18603

2020-12-21

Abstract:Polymer composites with highly thermally conductive and electrical insulation are urgently demanded for thermal management in modern electrical and energy applications. However, the incorporation of metal fillers in traditional polymeric composites usually fails to meet the requirements for simultaneously high thermal conductivity and high electrical insulation. Here, we successfully fabricated composites with high thermal conductivity and high electrical insulation by in situ thermal expansion of expandable graphite (EG) and in situ oxidation of aluminum (Al) nanoflakes in aluminum-plastic package waste (APPW). Due to the synergistic effect of the hybrid filler framework, the maximum thermal conductivity reached as high as 8.7 W m^–1 K^–1 for APPW/EG₁₀/Al₆₀-F composites. In addition, the formation of the nano Al₂O₃ layer around the Al filler surface brings extremely low electrical conductivity (&lt;10^–14 S cm^–1) and low dielectric loss (&lt;0.06). Based on the results of finite element simulation, the heat flowed mainly along the effective filler framework and the high thermal conductivity is attributed to the interconnection of the high aspect ratio filler. Furthermore, the strong thermal management capability of the prepared composites was demonstrated in the heat dissipation experiment. The present work suggests that surface-oxidized Al nanoflakes demonstrate fascinating performance and show promising application as thermal management materials in emerging electrical systems and electronic devices.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acsami.0c18603?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acsami.0c18603</a>.SEM images of expandable graphite (Figure S1); FTIR absorbance data of carbon dioxide in APPW/EG/Al-F composites (Figure S2); XRD pattern of the APPW/EG composite prepared by melt blend under 200 °C (Figure S3); TGA and DTG curves of APPW/EG/Al composites (Figure S4); SEM images of the fracture surface of composites (Figure S5); TEM images of graphite nanosheets in APPW/EG10/Al30-F composites (Figure S6); TEM images of as-received Al platelet (Figure S7); volume resistivity of APPW/EG composites (Figure S8); APPW/EG10/Al60-S at different cooling times at insulating foam within 1 min (Figure S9); dielectric permittivity and dielectric loss of composites at 1k Hz (Figure S10); dielectric permittivity, dielectric loss, and electric conductivity of composites at different temperatures at 1k Hz (Figure S11); list of samples and their codes for different EG and Al loadings (Table S1); calculated electrical conductivity, electronic thermal conductivity, and phonon thermal conductivity of composites (Table S2); major parameters used in the simulation (Table S3) (<a class="ext-link" href="/doi/suppl/10.1021/acsami.0c18603/suppl_file/am0c18603_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

materials science, multidisciplinary,nanoscience & nanotechnology