A Dual Physical Cross-Linking Strategy to Construct Tough Hydrogels with High Strength, Excellent Fatigue Resistance, and Stretching-Induced Strengthening Effect
Qianyu Yang,Chen Gao,Xuemei Zhang,Chihui Tsou,Xingyu Zhao,Manuel Reyes De Guzman,Zejun Pu,Xinyue Li,Yue Lu,Chunyan Zeng,Li Yuan,Yiqing Xia,Yuping Sheng,Yiqing Fu
DOI: https://doi.org/10.1002/mame.202100093
2021-01-01
Macromolecular Materials and Engineering
Abstract:Hydrogels with excellent stiffness, toughness, anti-fatigue, and self-recovery properties are regarded as promising water-containing materials. In this work, a dual physically cross-linked (DPC) sodium alginate (SA)/poly[acrylamide (AAm)-acrylic acid (AAc)-octadecyl methacrylate (OMA)]-Fe3+ hydrogel is reported, which is constructed by hydrophobic association (HA) and ionic coordination (IC). The optimal DPC hydrogel demonstrates excellent mechanical performance: tensile modulus of 0.65 MPa, tensile strength of 3.31 MPa, elongation at break of 1547%, and toughness of 27.8 MJ m(-3). SA/P(AAm-AAc-OMA)-Fe3+ DPC hydrogels also exhibit prominent anti-fatigue and self-recovery performance (99.1-109.7% modulus recovery and 90.4-108.9% dissipated energy recovery after resting for 5 min without additional stimuli at ambient temperature) through the reconstruction of reversible physical cross-linking. Some of the SA/P(AAm-AAc-OMA)-Fe3+ DPC hydrogels even exhibit a stretching-induced strengthening effect, which is similar to the performance of muscle-"the more training, the more strength." Hence, the combination of HA and IC will provide an effective approach to design DPC hydrogels with desirable mechanical performances and a longer service life for wider applications of soft materials.