Sustained release of a thiosemicarbazone from antibacterial electrospun poly(lactic‐co‐glycolic acid) fiber mats

Hossein Barani,Alexander Haseloer,Sanjay Mathur,Axel Klein

DOI: https://doi.org/10.1002/pat.5043

IF: 3.348

2020-07-28

Polymers for Advanced Technologies

Abstract:<p>Antibacterial fiber mats of poly(lactic‐co‐glycolic acid) (PLGA) were produced in the presence of different amounts of the thiosemicarbazone (TSC) <i>N </i>4‐(<i>S </i>)‐(1‐phenylethyl)‐2‐(pyridin‐2‐ylmethylene)hydrazine‐1‐carbothioamide (HfpyTSCmB) through electrospinning. Increasing amounts (0, 2.5, 5, and 10 wt%) of TSC in the PLGA spinning solution in 2,2,2‐trifluoroethanol (TFE) caused an increase up to 230% in conductivity and up to 27% in viscosity. The morphology of the electrospun fibers was studied using scanning electron microscope (SEM) and showed the formation of uniform, bead free, cylindrical, and smooth fiber mats. Increasing amounts of HfpyTSCmB in the polymer solution resulted also in significant shrinking of the diameter and narrowing of the size distribution of the fibers in line with the increased conductivity of the spinning solutions. Nuclear magnetic resonance (NMR) spectroscopy and thermal methods (DSC and TG/DTA) gave proof for the chemical integrity of HfpyTSCmB in the fiber mats after the electrospinning process. The release profile of HfpyTSCmB from the fibers was examined using UV‐vis absorption spectroscopy. The observed release data during 21 days was fitted to different mathematical models with the best results obtained from the Higuchi release model. The fiber mat samples showed effective antibacterial properties with inhibition zones of 0.5 to 1.5 mm against the Gram‐positive <i>Staphylococcus aureus </i> and the Gram‐negative <i>Escherichia coli </i>.</p>

polymer science

What problem does this paper attempt to address?

The main problem that this paper attempts to solve is to develop an antibacterial fiber mat with the ability to continuously release antibacterial agents. Specifically, the researchers used poly(lactic - co - glycolic acid) (PLGA) as the substrate and added different contents of pyridylthiosemicarbazone (HfpyTSCmB), and prepared antibacterial fiber mats by electrospinning technology. The main objectives of the study include:

1. **Improve drug - loading efficiency**: By adding different amounts of HfpyTSCmB to the PLGA solution, the researchers aimed to improve the drug - loading efficiency in the fibers, thereby achieving a higher antibacterial effect.

2. **Optimize fiber morphology**: The researchers explored the influence of different HfpyTSCmB contents on fiber morphology, especially the changes in fiber diameter and distribution. The results showed that as the HfpyTSCmB content increased, the fiber diameter decreased significantly and the distribution became more uniform.

3. **Evaluate drug - release characteristics**: By UV - Vis absorption spectroscopy, the researchers monitored the release of HfpyTSCmB from the fiber mat. The experimental data showed that the release of HfpyTSCmB conformed to the Higuchi model, that is, it was mainly released through the diffusion mechanism. In addition, as the HfpyTSCmB content increased, the cumulative release rate gradually decreased, which may be because the high - content HfpyTSCmB enhanced the stability of PLGA fibers and slowed down the hydrolysis process.

4. **Verify antibacterial properties**: The researchers evaluated the inhibitory effect of PLGA - TSC fiber mats on Staphylococcus aureus and Escherichia coli through in vitro antibacterial tests. The results showed that the fiber mats containing HfpyTSCmB exhibited a good inhibitory effect on both bacteria, and the inhibitory effect on Gram - positive bacteria was stronger.

In conclusion, this study aims to prepare PLGA fiber mats with the ability to continuously release antibacterial agents by electrospinning technology to meet the needs of combating drug - resistant pathogens and provide a reference for the development of new antibacterial materials.