Abstract:The current study highlights the corrosion consequences observed in API 5L X65 carbon steel when exposed to a marine-like environment containing carbon dioxide (CO2), in the presence of sulfate- reducing bacteria consortium (C-SRB), iron-reducing bacteria consortium (C-IRB), and a combination of both (C-SRB+C-IRB). The corrosion behaviour was assessed through the utilisation of weight loss and surface analysis techniques. The biofilms and corrosion products were characterised using field emission scanning electron microscopy (FESEM) and infinite focus microscope (IFM), respectively. The results obtained from the weight loss technique provided confirmation that in the absence of bacteria, uniform corrosion was the prevailing mechanism in the medium. The uniform corrosion rate was found to be 0.95 mm/year, which was higher than the pit penetration rate of 0.28 mm/year. The combined actions of the C-SRB+C-IRB consortium result in a synergistic impact, leading to a significantly higher rate of pit penetration compared to the individual activities of SRB. Specifically, the pit penetration rate value of 2.13 mm/year is observed, which is notably higher than the uniform corrosion rate of 0.59 mm/year. The utilisation of surface analysis techniques has shown evidence of the existence of sulfur on carbon steel samples that were subjected to exposure from the C-SRB+C-IRB consortium in a CO2 environment. This sulphur presence is believed to potentially play a role in the development of the iron sulphide (FeS) layer. FeS presence is a contributing factor to the occurrence of pit corrosion due to the SRB metabolite activities. The activities of these metabolites readily dissolve in the medium, hence altering the chemical interface properties of both the metal and the biofilm. For specimens exposed to C-SRB only, the results obtained were almost identical to exposure to the C- SRB+C-IRB consortium. However, the corrosion rate value measured for the C-SRB+C-IRB consortium was higher due to the synergistic effect of the two bacteria. In conclusion, the presence of C-SRB alone and the consortium of C-SRB+C-IRB in a CO2 environment induces the formation of pitting corrosion. The findings of this study are presumed to contribute a deep understanding of the microbiology-influenced corrosion (MIC) mechanism in CO2 environments troubling the oil and gas industry. With a better understanding of MIC, new and improved corrosion prevention strategies can be put into action.

Effect of ferrous sulfate treatment on microbially influenced corrosion of CuNi 70/30 marine pipeline alloy by sulfate reducing bacteria

Laboratory Investigation of the Microbiologically Influenced Corrosion (MIC) Resistance of a Novel Cu-bearing 2205 Duplex Stainless Steel in the Presence of an Aerobic Marinepseudomonas Aeruginosabiofilm

Influence of cu distribution in thermally sprayed cu-bearing coatings on the prevention of Desulfovibrio vulgaris corrosion

Effect of anodic polarization treatment on microbiologically influenced corrosion resistance of Cu-bearing stainless steel against marine Pseudomonas aeruginosa

Influence of copper distribution in thermally sprayed Cu-bearing coatings on corrosion and microbial activity

Laboratory investigation of the microbiologically influenced corrosion (MIC) resistance of a novel Cu-bearing 2205 duplex stainless steel in the presence of an aerobic marine Pseudomonas aeruginosa biofilm

Influence of Sulfate and Iron Reducing Bacteria on Carbon Steel Corrosion in Marine Environments

Role of Fe oxide in the underdeposit corrosion of pipeline steel in oilfield produced water containing SRB

Effect of Cu Addition in Pipeline Steels on Microstructure,Mechanical Properties and Microbiologically Influenced Corrosion

Influence of initial pH and sulfate‐reducing bacteria concentration on the microbiologically influenced corrosion of buried pipeline steel

Effect of Nano-sized Cu-Rich Phase on Microbiological Corrosion Behavior of Cu and Ni-Added Steel for Oil Country Tubular Goods

The Effect of Sufate-Reducing Bacteria and Iron Bacteria on Corrosion in Water Distribution Systems

Synergistic effect of carbon starvation and exogenous redox mediators on corrosion of X70 pipeline steel induced by Desulfovibrio singaporenus

Effect of Cu addition to AISI 8630 steel on the resistance to microbial corrosion

Effect of pH regulation by sulfate-reducing bacteria on corrosion behaviour of duplex stainless steel 2205 in acidic artificial seawater

Microbiologically influenced corrosion of FeCoNiCrMn high-entropy alloys by Pseudomonas aeruginosa biofilm

Inhibition Effect on Microbiologically Influenced Corrosion of Ti-6Al-4V-5Cu Alloy Against Marine Bacterium Pseudomonas Aeruginosa

Inhibition of microbial extracellular electron transfer corrosion of marine structural steel with multiple alloy elements

Microbiologically influenced corrosion of a novel pipeline steel containing Cu and Cr elements in the presence of Desulfovibrio vulgaris Hildenborough

Short- to medium-term corrosion of mild steel in highly calcareous seawaters: effects of calcium carbonate concentration, coupon orientation and nutrient addition

Corrosion Behavior of Cupronickel Alloy in Simulated Seawater in the Presence of Sulfate-Reducing Bacteria