Chemical Bath Deposition of NiFe Alloy Anode for Efficient Alkaline Water Electrolyzer Integration

Jingwen Wu,Zhibo Ren,Xindi Xu,Dong Hyeon Mok,Weiqi Guo,Ke Ye,Peng Shen,Weiyi Zhang,Baoxin Ni,Shusheng Wan,Gwonho Yu,Wen‐Bin Cai,Seoin Back,Jinyi Wang,Kun Jiang

DOI: https://doi.org/10.1002/smll.202407374

IF: 13.3

2024-10-28

Small

Abstract:A chemical bath deposition of homogeneous FeNi alloy catalyst is demonstrated within a flow reactor design, allowing for a batch synthesis of 5400‐cm2 Ni mesh supported FeNi3 anode within 4 min. Once integrated into water electrolyzer stack, these as‐prepared anodes drive an efficient and stable alkaline water splitting performance at industrial‐level current densities. Green hydrogen production from water splitting is a feasible way for intermittent renewable energy storage and utilization, where the exploration and scale‐up preparation of high‐performance anodic oxygen evolution electrocatalysts are critical prerequisites for its industrial‐level applications. Herein, a chemical bath deposition of FeNi3 intermetallic alloys onto Ni mesh support is performed, which delivers a current density of 0.62 A cm−2 at 1.72 V versus reversible hydrogen electrode for alkaline water oxidation in 1 m KOH and an excellent electrolysis stability at 0.2 A cm−2 for over 300 h. Moreover, via 3D computational fluid dynamics simulation and flow field optimization, a homogeneous deposition of ≈5400 cm2 NiFe anode is demonstrated within 4 min using the developed flow bath reactor. Once integrating the as‐prepared NiFe anodes into alkaline electrolyzer stack, the voltage variation between each unit cell is below 40 mV at a total operation current of 71 A, or ca. current density of 0.2 A cm−2, confirming the uniformity of this batch synthesis protocol and its great potential for industrial alkaline water electrolysis.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology