Rolling contact fatigue deformation mechanisms of nickel-rich nickel-titanium-hafnium alloys

Sean H. Mills,Christopher Dellacorte,Ronald D. Noebe,Behnam Amin-Ahmadi,Aaron P. Stebner

DOI: https://doi.org/10.1016/j.actamat.2021.116784

IF: 9.4

2021-05-01

Acta Materialia

Abstract:<p>The deformation mechanisms that dictate the tribological performances of heat treated Ni₅₅Ti₄₅, Ni₅₄Ti₄₅Hf₁ and Ni₅₆Ti₃₆Hf₈ alloys are revealed through rolling contact fatigue (RCF) testing and transmission electron microscopy (TEM) analyses. Analysis of worn samples that passed a 5×10⁸ cycle RCF runout condition shows that damage is primarily confined to deformation bands that propagate several hundred nanometers – to – several microns beneath the surface. These bands nucleate via localization of dislocation slip within the B2 austenite phase of the alloys. For the Ni₅₅Ti₄₅ and Ni₅₄Ti₄₅Hf₁ samples, further damage and eventual spall failures occur by shearing and dissolution of the strengthening Ni₄Ti₃ nanoprecipitates within the deformation bands, followed by nanocrystallization that sometimes includes stress-induced nucleation of B19′ nanocrystals. Eventually, complete amorphization occurs prior to fracture. The relative 15 – 25% increase in RCF contact stress performance of the Ni₅₆Ti₃₆Hf₈ alloy correlates with a more limited depth of damaged material beneath the wear surface; heavily damaged material beneath spall failure sites only extends 1.5 µm into the sample, compared to &gt; 6 µm for Ni₅₅Ti₄₅ and Ni₅₄Ti₄₅Hf₁ alloys. This superior RCF damage resistance of the Ni₅₆Ti₃₆Hf₈ alloy results from a lower fraction of B2 matrix phase (≤ 13 %) that is highly confined by both cubic Ni-rich NiTiHf and H-phase nanoprecipitates. Specifically, this microstructure limits the widths of deformation bands within the B2 austenite phase to less than the size of the strengthening nanoprecipitates, which in turn inhibits precipitate shearing and dissolution processes that precede nanocrystallization and amorphization.</p>

materials science, multidisciplinary,metallurgy & metallurgical engineering