Synergistic Structure and Iron‐Vacancy Engineering Realizing High Initial Coulombic Efficiency and Kinetically Accelerated Lithium Storage in Lithium Iron Oxide

Naiteng Wu,Jinke Shen,Kai Yong,Chengqian Chen,Jian Li,Yi Xie,Donglei Guo,Guilong Liu,Jin Li,Ang Cao,Xianming Liu,Hongyu Mi,Hao Wu
DOI: https://doi.org/10.1002/advs.202206574
IF: 15.1
2023-01-23
Advanced Science
Abstract:A hollow slender carambola‐like Li0.43FeO1.51 with Fe vacancies is constructed via a facile reaction between metal–organic framework (MOF) precursor and Li2CO3. The in situ generated Fe vacancies are powerful for modulating the electronic structure to accelerate the transport rate of lithium ions and catalyze more decomposition of Li2O to participate in the reaction with Fe, finally enhancing the initial coulombic efficiency and rate performance of lithium iron oxide anode material. Transition metal oxides with high capacity still confront the challenges of low initial coulombic efficiency (ICE, generally <70%) and inferior cyclic stability for practical lithium‐storage. Herein, a hollow slender carambola‐like Li0.43FeO1.51 with Fe vacancies is proposed by a facile reaction of Fe3+‐containing metal–organic frameworks with Li2CO3. Synthesis experiments combined with synchrotron‐radiation X‐ray measurements identify that the hollow structure is caused by Li2CO3 erosion, while the formation of Fe vacancies is resulted from insufficient lithiation process with reduced Li2CO3 dosage. The optimized lithium iron oxides exhibit remarkably improved ICE (from 68.24% to 86.78%), high‐rate performance (357 mAh g−1 at 5 A g−1), and superior cycling stability (884 mAh g−1 after 500 cycles at 0.5 A g−1). Paring with LiFePO4 cathodes, the full‐cells achieve extraordinary cyclic stability with 99.3% retention after 100 cycles. The improved electrochemical performances can be attributed to the synergy of structural characteristics and Fe vacancy engineering. The unique hollow structure alleviates the volume expansion of Li0.43FeO1.51, while the in situ generated Fe vacancies are powerful for modulating electronic structure with boosted Li+ transport rate and catalyze more Li2O decomposition to react with Fe in the first charge process, hence enhancing the ICE of lithium iron oxide anode materials.
materials science, multidisciplinary,nanoscience & nanotechnology,chemistry
What problem does this paper attempt to address?