Abstract:Herein, we present the results of an experimental study on the mechanical properties of Fe-C alloys with different carbon contents (0.2, 0.45, and 0.8%) in a wide range of deformation rates (10−3–103 s−1) and abrasive wear resistance, which underwent combined laser thermal (laser surface hardening—LSH) and laser shock wave (Laser Shock Peening—LSP) processing. The combined treatment modes included a different sequence of exposure to laser thermal and laser-induced shock pulses on the material. The amplitude and duration of laser-induced shock waves were measured using a laser Michelson interferometer. The mechanical properties of steel samples were studied under conditions of uniaxial tension under static loads on a standard universal testing machine, the LR5KPlus, and under dynamic loading, tests were carried out on a specialized experimental complex according to the H. Kolsky method using a split Hopkinson rod. The abrasive wear resistance of hardened surfaces was studied using the Brinell–Haworth method. Studies have shown that the use of a combination of LSH and LSP treatments leads to an increase in both the mechanical properties of steels and abrasive wear resistance compared to traditional laser hardening. It has been established that in the combinations considered, the most effective is laser treatment, in which LSP treatment is applied twice: before and after LSH. Thus, after processing steels using this mode, an increase in the depth of the hardened layer was recorded—by 1.53 times for steel 20, by 1.41 times for steel 45, and by 1.29 times for steel U8—as well as a maximum increase in microhardness values by 22% for steel 20, by 27% for steel 45, and by 13% for U8 steel. The use of this mode made it possible to obtain the maximum strength properties of the studied materials under static and dynamic loading, which is associated with an increase in the volume fraction of the strengthened metal and high microhardness values of the strengthened layer of traditional LSH. The dependences of abrasive wear of the studied steels after various combinations of LSP and LSH impacts were established. It is shown that the greatest wear resistance of the studied steels is observed in the case when the LSH pulse is located between two LSP pulses. In this case, abrasive wear resistance increases by 1.5–2 times compared to traditional LSH.

Effect of Laser Processing on Impact Resistance of Steel Coating

Effect of Combined Laser Thermal and Shock Wave Effects on the Mechanical and Tribological Properties of Steels

The Effect of Laser Beam Processing on the Properties of WC-Co Coatings Deposited on Steel

Influence of the initial structure on the efficiency of laser processing of steel

Impact of Laser Shock Processing on Microstructure and Tribological Performance of GCr15 Bearing Steel

Effects of Laser Shock Processing on Morphologies and Mechanical Properties of ANSI 304 Stainless Steel Weldments Subjected to Cavitation Erosion

Laser shock peening on high-strength steel

Features of Steel Structure Formation in Areas of High-Speed Laser Hardening from Liquid State

Effects of laser additive manufacturing on microstructure and crystallographic texture of austenitic and martensitic stainless steels

Effect of surface nanocrystallization produced by laser shock processing on the corrosion fatigue behavior of 300M steel

Effect of Nanosecond Laser Texturization on Tribological Behavior of AISI 321 Stainless Steel

Effect of Thermal Fields on the Structure of Corrosion-Resistant Steels Under Different Modes of Laser Treatment

High energy laser-shock induced phase transformation and micro-spallation on surface of stainless steels: The effect of stacking fault energy and deformation mechanisms

Aspects of Structure and Properties Formation in Steels During Laser-Acoustic Processing

Microstructure effect on sliding wear of 316L stainless steel selectively laser melted

Influence of Surface Modifications by Laser Shock Processing on the Acid Chloride Stress Corrosion Cracking Susceptibility of AISI 304 Stainless Steel

Effect of Pulsed Laser Energy on Grain Morphology and Texture Characteristics of Stainless Steel Fabricated by Laser-Pta Additive Manufacturing

The Influence of Absorbing Coating Material on the Efficiency of Laser Shock Peening

Effect of laser shock peening on the retention ability of surface roughness in forged Cr5 steel

Local laser softening of press-hardened steel at high feed rates

Effect of asynchronized and synchronized laser shock peening on microstructure and mechanical properties of the Ti-6Al-4V laser joint