Abstract:Phosphogypsum is an industrial waste generated in the production of fertilizers causing environmental problems. Calcined phosphogypsum (CPG) is obtained by low-temperature calcination and dehydration of phosphogypsum. CPG is mainly used to produce building materials. However, mechanical strength properties and water resistance of CPG materials is extremely poor, which leads to its relatively low utilization rate in construction industry. To address this issue, various amount of Ordinary Portland cement (OPC), fly ash (FA), rice husk (RH) and modified admixtures (AD) were mixed with the CPG to obtain CPG-based composite cementitious materials, which enhanced the water resistance and mechanical strength of the corresponding hardened materials. The influence of different contents of cement on the setting time, hydration heat, hydration products, mechanical properties, water absorption, heavy metal leaching and deterioration coefficient of the composite cementitious material is investigated. The results showed that the optimal mixing ratio of CPG: OPC: FA: RH was 57: 20: 10: 13 considering the water resistance and mechanical strength properties of CPG-based composite cementitious materials. On these conditions, the compressive strength, the flexural strength, water absorption and deterioration coefficient of the specimens at 28 days are 6.1 MPa, 4.6 MPa, 29.4% and 0.66 respectively, which were in line with the national standard of phosphorus building gypsum wallboard. It was demonstrated that two skeleton types are present in the samples prepared using CPG-based composite cementitious materials, which had a synergistic support effect on the structure. The first skeleton was formed by gypsum dihydrate crystals (CaSO 4 ·2H 2 O) and provided strength to the specimens at an early stage, while the second skeleton was formed by ettringite (AFt) and C–S–H gels, which provided strength at a later stage. The skeletons make the hardened materials denser and more waterproof. Moreover, the composite materials exhibited a positive solidification effect on heavy metals present in CPG.

Phosphogypsum valorization in cement: Experimental study of the PG effect and the water-to-cement ratio on the flexural strength of cement paste

Potential use of phosphogypsum in concrete

Thermal and Mechanical Properties Enhancement of Cement Mortar using Phosphogypsum Waste: Experimental and Modeling Study

Study on the Mechanical Properties, Microstructure and Hydration Mechanism of Phosphogypsum-Based Geopolymer Cement with Added Micron-Sized Silica Particles

Development and optimization of phosphogypsum-based geopolymer cement

Valorization of phosphogypsum as a road material: Stabilizing effect of fly ash and lime additives on strength and durability

Valorization of phosphogypsum as hydraulic binder

Enhancing Compressive Strength of Phosphogypsum-Based Geopolymer Cement with Five Alkaline Activator Combinations

Influence of treated waste phosphogypsum materials on the properties of ordinary portland cement

Effect of Phosphogypsum on the Properties of Portland Cement

Influence of cement on properties of calcined phosphogypsum based composite cementitious materials

The Development of a New Phosphogypsum-Based Construction Material: A Study of the Physicochemical, Mechanical and Thermal Characteristics

Investigation on the preparation of low carbon cement materials from industrial solid waste phosphogypsum: Clinker preparation, cement properties, and hydration mechanism

Effects of phosphogypsum on hydration properties and strength of calcium aluminate cement

Characterization and purification of waste phosphogypsum to make it suitable for use in the plaster and the cement industry

The effects of admixtures on the durability properties of phosphogypsum-based cementitious materials

Research on the Application of Phosphogypsum in Magnesium Oxysulfate Cement: A Comparison with Sand

Preparation of Foamed Phosphogypsum Lightweight Materials by Incorporating Cementitious Additives

Improvement of physico-mechanical and microstructural properties of magnesium phosphate cement composites comprising with Phosphogypsum

Influences of pretreatment methods on the mechanical and environmental behaviors of PG-GGBS-LM ternary stabilizer

A Sustainable Composite Cementitious Material Manufactured by Phosphogypsum Waste