Effects of Thermal Damage on Impact Response Characteristics of High-Energy Propellants

Fengwei Guo,Jianxin Nie,Suoshuo Zhang,Jiahao Liang,Rui Liu,Yu Zou,Yong Han

DOI: https://doi.org/10.3390/polym16060748

IF: 5

2024-03-09

Polymers

Abstract:Thermal damage due to microstructure changes will occur in propellants under thermal stimulation. It can significantly affect the sensitization, combustion, and other properties of the propellant, which, in turn, affects the impact safety of the solid propellant rocket engine. A new component which uniformly heats the sample was designed to conduct the Lagrange test and EFP impact test at different temperatures. The thermal decomposition and damage characteristics of the propellant during the heating process were quantitatively analyzed. Additionally, the effects of ambient temperature on impact initiation and detonation growth of the high-energy propellant were elucidated at a mesoscopic level. The results showed that the porosity of the specimen increased by 0.89% under the thermomechanical mechanism, which was mainly characterized by interfacial de-bonding between the AP and the binder. The increase in thermal damage changed the hot spot reaction rate and significantly affected the growth process of propellant impact initiation. A method was proposed to systematically calibrate the reaction rate model for the propellant at different temperatures. The theoretical model parameters of the high-energy propellant at two typical temperatures were calibrated in this way. The critical shell thicknesses computed using LS-DYNA, which, for 20 and 70 °C, were obtained as 15 and 20 mm, respectively.

polymer science

What problem does this paper attempt to address?

The paper aims to study the impact of thermal damage on the shock response characteristics of high-energy propellants. Specifically, the paper focuses on the effect of thermal stimulation at different temperatures on the microstructural changes of the propellant. These changes significantly affect the sensitivity, combustion performance, and other characteristics of the propellant, thereby influencing the shock safety of solid propellant rocket engines. To investigate this issue, the authors designed a new component to uniformly heat the samples and conducted Lagrangian tests and EFP shock tests at different temperatures. Through these experiments, the thermal decomposition and damage characteristics of the propellant during heating were quantitatively analyzed, and the impact of ambient temperature on the shock initiation and detonation wave growth of high-energy propellants was elucidated.

The study found that under the thermo-mechanical mechanism, the porosity of the sample increased by 0.89%, mainly due to the debonding at the interface between ammonium perchlorate (AP) and the binder. The increase in thermal damage altered the hotspot reaction rate and significantly affected the shock initiation process of the propellant. Therefore, a method was proposed to systematically calibrate the reaction rate model of the propellant at different temperatures, and the theoretical model parameters of the high-energy propellant were calibrated at two typical temperatures (20°C and 70°C). The critical shell thicknesses obtained using LS-DYNA calculations were 15 mm and 20 mm, respectively. These results provide important references for evaluating the safety of high-energy propellants and optimizing their design.