CuCoO2 nanocrystals derived from an isopropanol modified Cu-BTC using in alkaline water oxidation

Shiyu Ma,Miao Yang,Na Han,Lifen Shi,Liang Wang,Jilin Bai,Dehua Xiong
DOI: https://doi.org/10.1039/d3nj00059a
IF: 3.3
2023-02-12
New Journal of Chemistry
Abstract:In this work, CuCoO2 (CCO) nanocrystals were derived from the Cu-BTC/Cu-BTC-IPA precursors through solvothermal method at 140 °C, and the electrocatalytic oxygen evolution reaction (OER) application of CCO catalysts were investigated. Firstly, the optimized Cu-BTC-IPA precursor was prepared through the hydrothermal reaction at 120 °C with 9 ml isopropyl alcohol (IPA) addition. IPA species can affect the morphology and composition of CCO nanocrystals by tailoring the structure of bare Cu-BTC, resulting in the Cu-BTC-IPA derived CCO2 nanocrystals have a smaller grain size of 110 nm and a larger specific surface area of 9.78 m2 g-1, which is in comparison to than that of Cu-BTC derived CCO1 nanocrystals. Secondly, the Ni@CCO2 electrode required an overpotential of 467 mV to reach 10 mA cm-2, which is much lower than that of Ni@CCO1 electrode (i.e. 493 mV). The Ni@CCO2 electrode also exhibits a small overpotential degradation of only 20 mV after 18 hours OER stability test, the measurement results confirmed that CCO2 catalyst has an excellent stability in structure and composition during long-term OER electrolysis. This work reveals the preparation method of CCO electrocatalyst by tailoring the organic ligands of MOFs precursors, supplying a new approach for the preparation of delafossite oxide CCO and the enhancement of their OER performances.
chemistry, multidisciplinary
What problem does this paper attempt to address?